Acta Metallurgica Sinica (English Letters) ›› 2012, Vol. 25 ›› Issue (2): 89-94.DOI: 10.11890/1006-7191-122-89

    Next Articles

Effect of parameters on interface of the brazed ZrO2 ceramic and Ti-6Al-4V joint using Ti-based amorphous filler

Yuhua LIU1, Jiandong HU1, Yaping ZHANG1, Zuoxing GUO1, Yue YANG2   

  1. 1. Key Laboratory of Automobile Materials, Ministry of Education, College of Materials Science and Engineering, Jilin University, Changchun 130025, China
    2. Key Laboratory of Advanced Structural Materials, Ministry of Education, Changchun University of Technology, Changchun 130012, China
  • Received:2011-09-16 Revised:2011-11-12 Online:2012-04-25 Published:2012-04-11
  • Contact: Zuoxing GUO

Abstract: A commercially available Ti47Zr28Cu14Ni11 (at. pct) amorphous filler foil was used to join ZrO2 ceramic and Ti-6Al-4V alloy. According to experimental observations, the interface microstructure accounts for the mechanical properties of the joints. The effects of brazing conditions and parameters on the joint properties were investigated. The joint shear strength showed the highest value of about 108 MPa and did not monotonously increase with the brazing time increasing. It was shown that decreasing of brazing cooling rate and appropriate filler foil thickness gave higher joint strength.

Key words: Brazing, Amorphous filler, Brazing parameter, Interface microstructure, Shear strength