CRACK INITIATION AND STEADY PROPAGATION OF ELASTIC-PLASTIC MATERIALS IN PLANE STRESS CONDITION

Abstract

Abstract: The crack tip stress-strain fields of the elastic-plastic cracked specimens have been analyzed using finite element calculations.The crack initiation and steady propagation behaviours have also been investigated by means of slip line pattern etching technique and mechanical tests. The results show that there are HRR near field and distant field in the crack tip region,and the later depends on the specimen configuration.The crack initiation behaviour is controlled by a single parameter J.In contrast,the steady crack propagation is affected by the distant strain field and can not be described by single parameter only.

Key words: plane stress, elastic-plastic material, crack propagation, steel 00Cr14Ni14Si4

ZHUANG Tao WANG Zhongfang Central Iron and Steel Research Institute,Ministry of Metallurgical Industry,Beijing Dept.No.13,Central Iron and steel Research Institute,Ministry of Metallurgical Industry,Beijing,China. CRACK INITIATION AND STEADY PROPAGATION OF ELASTIC-PLASTIC MATERIALS IN PLANE STRESS CONDITION[J]. Acta Metallurgica Sinica (English Letters), 1989, 2(5): 354-358.

[1]	Ke Xu, Tao Fang, Longfei Zhao, Haichao Cui, Fenggui Lu. Effect of Trace Element on Microstructure and Fracture Toughness of Weld Metal [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(3): 425-436.
[2]	Rong-Hua Li, Peng Zhang, Zhe-Feng Zhang. Torsional Fatigue Cracking and Fracture Behaviors of Cold-Drawn Copper: Effects of Microstructure and Axial Stress [J]. Acta Metallurgica Sinica (English Letters), 2019, 32(12): 1521-1529.
[3]	Noritake Hiyoshi. Crack Initiation and Propagation Evaluation for Sn-5Sb Solder Under Low-Cycle Fatigue [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(9): 851-856.
[4]	Meng Wang, Zhen-Yu Liu, Cheng-Gang Li. Correlations of Ni Contents, Formation of Reversed Austenite and Toughness for Ni-Containing Cryogenic Steels [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(3): 238-237.
[5]	Yun-Long Xue, Shuang-Ming Li, Hong Zhong, Lai-Ping Li, Heng-Zhi Fu. Microstructure Characterization and Fracture Toughness of Laves Phase-Based Cr-Nb-Ti Alloys [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(4): 514-520.
[6]	Galina Lasko, Ulrich Weber, Siegfried Schmauder. Finite Element Simulations of Crack Propagation in Al₂O₃/6061Al Composites [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(5): 853-861.
[7]	Bing JIANG, Yusong LIU,Meicheng LI. In-situ Observation of Crack Growth and Domain Switching Around Vickers Indentation on BaTiO₃ Single Crystal Under Sustained Electric Field [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(6): 772-776.
[8]	Masood Shah, Catherine Mabru, Farhad Rezai-Aria, Ines Souki,Riffat Asim Pasha. An estimation of stress intensity factor in a clamped SE(T) specimen through numerical simulation and experimental verification: case of FCGR of AISI H11 tool steel [J]. Acta Metallurgica Sinica (English Letters), 2012, 25(4): 307-319.
[9]	Z.J. Xu, Y.L. Li. A NOVEL METHOD FOR EVALUATING PLANE STRESS DYNAMIC FRACTURE TOUGHNESS OF 0Cr18Ni10Ti STAINLESS STEEL WELDED JOINTS [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(4): 303-312 .
[10]	Author X.S. Xie, Z.C. Xu and J.X. Dong High Temperature Materials Research Laboratory,University of Science and Technology Beijing,Beijing 100083, ChinaManuscript received 18 October 1998. HIGH TEMPERATURE CRACK PROPAGATION AND FRACTUREOF SUPERALLOYS [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(1): 54-61.
[11]	Z.X. Wu and X.F. Sun ( Institute of Applied Mechanics, Southwest Jiaotong University, Chengdu 610031, China State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China). BEHAVIOR OF SHORT FATIGUE CRACKS AT BLUNT NOTCHESIN A MEDIUM CARBON STEEL [J]. Acta Metallurgica Sinica (English Letters), 1997, 10(5): 430-436.
[12]	K.M. Chang(Department of Mechanical and Aerospace Engineering,West Virginia University, P.O. Box 6160, Morgantown,WV 26506, USA Manuscript received 26 August 1996). CRITICAL ISSUES OF POWDER METALLURGY TURBINE DISKS [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(6): 467-471.
[13]	W Liang~1,2), Q. Li~2) and D.ZYang~2)(Centre of Measuring and Testing Taiyuan University of Technology, Taiyuan 030024, China Institute of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 China Manuscript received 13 November 1995). AN IN SITU STUDY ON DEFORMATION TWINNING NEAR CRACK TIP IN TWO-PHASE TiAl-BASE ALIOY [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(4): 272-278.
[14]	WU Zhixue;XU Hao(Institute of Mechanical Engineering,Northeastern University,Shenyang 110006,China)(Fushun Petroleum institute,Fushun 113001.China).(State Key Laboratory for Fatigue and Fracture of Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110015,China) Manuscript received 2 July 1995. BEHAVIOUR OF INITIATION AND GROWTH OF SHORT FATIGUE CRACKS [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(1): 65-70.
[15]	SUN Jian ZHANG Yuanhu HU Gengxiang Shanghai Jiaotong University,Shanghai,China SUN Jian,lecturer,Department of Materials Science,Shanghai Jiaotong University,Shanghai 200030,China. CREEP CRACK PROPAGATION IN CONVENTIONAL CAST AND DIRECTIONALLY SOLIDIFIED SUPERALLOY RENE 80 [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(5): 343-345.

CRACK INITIATION AND STEADY PROPAGATION OF ELASTIC-PLASTIC MATERIALS IN PLANE STRESS CONDITION

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments