INFLUENCE OF GRAIN SHAPE AND CARBIDE ON CREEP CRACK GROWTH IN HK40

Abstract

Abstract: The influence of two different grain shapes and carbides in the HK40 alloy,the material for use of furnace tube,on the rate of creep crack growth has been investigated.The resistance to creep crack growth of the material with columnar grains is inferior than that with equiaxial grains when the load line is perpendicular to the columnar grain axis.The influence of secon- dary carbide on the rate of creep crack propagation depends upon the Brain shape.

Key words: grain shape, creep rate, crack propagation

ZHU Shijie Institute of Metal Research,Academia Sinica,Shenyang,China ZHAO Jie Fushun Institute of Petrochemistry,Fushun,China WANG Fugang Dalian University of Technology,Dalian,China Institute of Metal Research,Academia Sinica,Shenyang 110015. INFLUENCE OF GRAIN SHAPE AND CARBIDE ON CREEP CRACK GROWTH IN HK40[J]. Acta Metallurgica Sinica (English Letters), 1990, 3(6): 449-452.

[1]	Ke Xu, Tao Fang, Longfei Zhao, Haichao Cui, Fenggui Lu. Effect of Trace Element on Microstructure and Fracture Toughness of Weld Metal [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(3): 425-436.
[2]	Rong-Hua Li, Peng Zhang, Zhe-Feng Zhang. Torsional Fatigue Cracking and Fracture Behaviors of Cold-Drawn Copper: Effects of Microstructure and Axial Stress [J]. Acta Metallurgica Sinica (English Letters), 2019, 32(12): 1521-1529.
[3]	Noritake Hiyoshi. Crack Initiation and Propagation Evaluation for Sn-5Sb Solder Under Low-Cycle Fatigue [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(9): 851-856.
[4]	Meng Wang, Zhen-Yu Liu, Cheng-Gang Li. Correlations of Ni Contents, Formation of Reversed Austenite and Toughness for Ni-Containing Cryogenic Steels [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(3): 238-237.
[5]	Yun-Long Xue, Shuang-Ming Li, Hong Zhong, Lai-Ping Li, Heng-Zhi Fu. Microstructure Characterization and Fracture Toughness of Laves Phase-Based Cr-Nb-Ti Alloys [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(4): 514-520.
[6]	Galina Lasko, Ulrich Weber, Siegfried Schmauder. Finite Element Simulations of Crack Propagation in Al₂O₃/6061Al Composites [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(5): 853-861.
[7]	Bing JIANG, Yusong LIU,Meicheng LI. In-situ Observation of Crack Growth and Domain Switching Around Vickers Indentation on BaTiO₃ Single Crystal Under Sustained Electric Field [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(6): 772-776.
[8]	Masood Shah, Catherine Mabru, Farhad Rezai-Aria, Ines Souki,Riffat Asim Pasha. An estimation of stress intensity factor in a clamped SE(T) specimen through numerical simulation and experimental verification: case of FCGR of AISI H11 tool steel [J]. Acta Metallurgica Sinica (English Letters), 2012, 25(4): 307-319.
[9]	Author X.S. Xie, Z.C. Xu and J.X. Dong High Temperature Materials Research Laboratory,University of Science and Technology Beijing,Beijing 100083, ChinaManuscript received 18 October 1998. HIGH TEMPERATURE CRACK PROPAGATION AND FRACTUREOF SUPERALLOYS [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(1): 54-61.
[10]	S.H.Ai,Y.B.Xia and J.F.Tian (State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110015, China). THE CREEP AND FRACTURE BEHAVIOR OF TWO NICKEL-BASED SUPERALLOYS [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(6): 425-428.
[11]	Z.X. Wu and X.F. Sun ( Institute of Applied Mechanics, Southwest Jiaotong University, Chengdu 610031, China State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China). BEHAVIOR OF SHORT FATIGUE CRACKS AT BLUNT NOTCHESIN A MEDIUM CARBON STEEL [J]. Acta Metallurgica Sinica (English Letters), 1997, 10(5): 430-436.
[12]	K.M. Chang(Department of Mechanical and Aerospace Engineering,West Virginia University, P.O. Box 6160, Morgantown,WV 26506, USA Manuscript received 26 August 1996). CRITICAL ISSUES OF POWDER METALLURGY TURBINE DISKS [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(6): 467-471.
[13]	W Liang~1,2), Q. Li~2) and D.ZYang~2)(Centre of Measuring and Testing Taiyuan University of Technology, Taiyuan 030024, China Institute of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 China Manuscript received 13 November 1995). AN IN SITU STUDY ON DEFORMATION TWINNING NEAR CRACK TIP IN TWO-PHASE TiAl-BASE ALIOY [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(4): 272-278.
[14]	WU Zhixue;XU Hao(Institute of Mechanical Engineering,Northeastern University,Shenyang 110006,China)(Fushun Petroleum institute,Fushun 113001.China).(State Key Laboratory for Fatigue and Fracture of Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110015,China) Manuscript received 2 July 1995. BEHAVIOUR OF INITIATION AND GROWTH OF SHORT FATIGUE CRACKS [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(1): 65-70.
[15]	TIAN Baohong ZHENG Shi'an WU Lei Luoyang Institute of Technology,Luoyang,China ZHENG Shi'an,associate professor,Department of Materials Engineering,Luoyang Institute of Technology,Luoyang 471039,China. FATIGUE BEHAVIOUR OF M/B DUPLEX STRUCTURE IN A HIGH CARBON Cr-Mo-W STEEL [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(5): 316-319.

INFLUENCE OF GRAIN SHAPE AND CARBIDE ON CREEP CRACK GROWTH IN HK40

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments