SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS

Acta Metallurgica Sinica (English Letters) ›› 1990, Vol. 3 ›› Issue (4): 276-281.

• Research paper • Previous Articles Next Articles

SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS

HOGN Youshi LU Yonghua ZHENG Zhemin Institute of Mechanics,Academia Sinica,Beijing,China Institute of Mechanics,Academia Sinica,Beijing 100080,China

Received:1990-08-25 Revised:1990-08-25 Online:1990-08-25 Published:2009-10-10

Abstract

Abstract: Fatigue tests were made on a vibration machine using specially designed specimens to investi- gate the initiation and propagation features of short fatigue cracks in a weld metal.The spec- imens were triangular in shape so that when loaded as a cantilever beam the surface tensile stress is constant.Test results show that short fatigue cracks mainly originate from slip bands within ferrite grains.The development of short fatigue cracks is marked by a gradual increase in crack density with fatigue cycles.Coalescence of short cracks leads to crack propagation and the crack path is predominantly transgranular.

Key words: iso—stress specimen, short fatigue crack, weld metal

HOGN Youshi LU Yonghua ZHENG Zhemin Institute of Mechanics,Academia Sinica,Beijing,China Institute of Mechanics,Academia Sinica,Beijing 100080,China. SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS[J]. Acta Metallurgica Sinica (English Letters), 1990, 3(4): 276-281.

[1]	Ke Xu, Tao Fang, Longfei Zhao, Haichao Cui, Fenggui Lu. Effect of Trace Element on Microstructure and Fracture Toughness of Weld Metal [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(3): 425-436.
[2]	Reza Nakhaei, Alireza Khodabandeh, Hamidreza Najafi. Effect of Active Gas on Weld Shape and Microstructure of Advanced A-TIG-Welded Stainless Steel [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(3): 295-300.
[3]	Xin WANG, Wenchao DONG, Shanping LU, Guangzhong HE, Xu ZHAO, Dianmai ZHOU, Yiyi LI. Effects of Ti-bearing inclusions on the microstructure and mechanical properties of MAG multilayer weld metal [J]. Acta Metallurgica Sinica (English Letters), 2012, 25(1): 1-9.
[4]	Ming WU, Xu CHEN, Chuan HE, Jun XIAO. Effect of CO₂ partial pressure on SCC behavior of welded X80 pipeline in simulated soil solution [J]. Acta Metallurgica Sinica (English Letters), 2011, 24(1): 65-74.
[5]	H.Hongo. EVALUATION OF CREEP PROPERTIES FOR 316FR STEEL THICK PLATE WELDMENT USING MINIATURE CREEP SPECIMEN [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(4): 369-374 .
[6]	Q. Gao; Y.X. Zhao and L.X. Cai (Institute of Applied Mechanics, Southwest Jiaotong University, Chengdu 610031, China). A PROBABILISTIC ASSESSMENT OF TEMPERATURE EFFECTS ON THE LOW CYCLE FATIGUE BEHAVIOUR OF 1Cr_(18)Ni_9Ti STEEL WELD METAL [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(6): 477-484.
[7]	Z.L. Zhou and S.H. Liu(Dept. of Materials Science and Engineering, Dalian Railway Institute, Dalian 116028, China). INFLUENCE OF LOCAL BRITTLE ZONE ON THE FRACTURE TOUGHNESS OF HIGH-STRENGTH LOW-ALLOYED MULTIPASS WELD METALS [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(2): 87-92.
[8]	Z.X. Wu and X.F. Sun ( Institute of Applied Mechanics, Southwest Jiaotong University, Chengdu 610031, China State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China). BEHAVIOR OF SHORT FATIGUE CRACKS AT BLUNT NOTCHESIN A MEDIUM CARBON STEEL [J]. Acta Metallurgica Sinica (English Letters), 1997, 10(5): 430-436.
[9]	ZANG Qishan LIU Kang Institute of Metal Research,Academia Sinica,Shenyang,ChinaKE Wei ZHENG Yuli Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China. CRACK GROWTH RATE IN WELD METAL OF HOMEMADE OFFSHORE STRUCTURE STEEL 36Z [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(8): 99-103.
[10]	CHEN Zheng Northwestern Polytechnical University,Xi′an,China Lab.No.401,Northwestern Polytechnical University,Xi′an 710072. THRESHOLD OF SHORT FATIGUE CRACK FOR Al-Li ALLOY 8090 [J]. Acta Metallurgica Sinica (English Letters), 1991, 4(2): 135-138.
[11]	PEI Hongxun YANG Jingjun KE Wei Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China PEI Hongxun Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China. GROWTH OF SHORT CRACKS OF A537CLI STEEL UNDER FATIGUE LOADING IN 3.5% NaCl SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1989, 2(9): 167-171.

SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 11

Recommended Articles

Metrics

Comments