High Temperature Oxidation of FGH96 P/M Superalloy

Acta Metallurgica Sinica (English Letters) ›› 2007, Vol. 20 ›› Issue (2): 102-110 .

• Research Articles • Previous Articles Next Articles

High Temperature Oxidation of FGH96 P/M Superalloy

F.J. Liu, M.C. Zhang, J.X. Dong, and Y.W. Zhang

School of Materials Science and Engineering, University of Science and Technology Beijing

Received:2006-06-28 Revised:2006-09-19 Online:2007-04-25 Published:2009-10-10

Abstract

Abstract: High temperature oxidation behaviors of FGH96 P / M superalloy have been studied in air at temperatures ranging from 600 to 1000℃. By means of isothermal oxidation testing, X-ray diffraction, SEM (scanning electron microscopy) and EDS (energy dispersive X-ray spectroscopy) analyses, the oxidation kinetics as well as the composition and morphology of scales were investigated. Thermodynamic calculations were used to explain the oxidation mechanism. The results showed that as the oxidation temperature increased, the oxidation rate, the scale thickness and scale spallation increased. FGH96 P / M superalloy exhibits good oxidation resistance at temperature below 800℃. The oxidation kinetics follows an approximately parabolic rate law, and the oxide layer was mainly composed of Cr2O3, TiO2, and a little amount of NiCr2O4. The oxidation is controlled by the transmission of chromium, titanium, and oxygen through the oxide scale.

Key words: FGH96 P/M superalloy, high temperature oxidation, oxide scale

F.J. Liu, M.C. Zhang, J.X. Dong, Y.W. Zhang. High Temperature Oxidation of FGH96 P/M Superalloy[J]. Acta Metallurgica Sinica (English Letters), 2007, 20(2): 102-110 .

References

1 G.B. Viswanathan1, P. Sarosi1, and M. Henry, in Superalloys 2004, Proc. of the 2004 TMS Symp., eds. K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra, and S.Walston (TMS, Warrendale, 2004) p.173.
2 S.Y. Wang, H.Q. Li, and M.C. Zhang, Hot Working Technology6 (2002) 16 (in Chinese).
3 D.D. Whitis, in Superalloys 2004, Proc. of the 2004 TMS Symp., eds. K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra, and S. Walston (TMS, Warrendale, 2004) p.391.
4 Y.H. Liu, F.G. Li, and S.C. Wu, Acta Aeronautica et Astronautica Sinica 24 (2003) 278 (in Chinese).
5 Y.B. Ching, J.L. Yi, and H.K. Chun, Surface and Coatings Technology183 (2004) 74.
6 S. Sinharoy and S.L. Narasimhan, in Superalloys 2004, Proc. of the 2004 TMS Symp., eds. K.A.Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra, and S. Walston (TMS, Warrendale, 2004) p.623.
7 W. Gao, Z.W. Li, and Z. Wu, Intermetallics 10 (2002) 263.
8 W.M. Guo, D. Feng, and F.G. Zhang, Journal of Iron and Steel Research 14 (2002) 17 (in Chinese).
9 W.M. Guo, F.G. Zhang, and Y.W. Zhang, Powder Metallurgy Industry12 (2002) 30 (in Chinese).
10 C.F. Miller, G.W. Simmons, and R.P. Wei, Scripta Mater. 42 (2000) 227.
11 S.X. Zhao, X.S. Xie, and G.D. Smith, Surface and Coatings Technology185 (2004) 178.
12 M.J. Lia, X.F. Suna, and H.R. Guana, Surface and Coatings Technology185 (2004) 172.
13 R. Haugsrud, Materials Science and Engineering A 298 (2001) 216.
14 J. Kl!wer, U. Brill, and U. Heubner, Intermetallics 7 (1999) 1183.
15 F.H. Yuan, Y.S. Yoo, and C.Y. Jo, Surface and Coatings Technology 183 (2004) 106.
16 J.P. Calder"n, E.B. Figueroa, and J.G. Gonz#lez-Rodríguez, Materials Letters 38 (1999) 45.
17 D.P. Whittle. Applied Science, eds. D. Coutsouradis, P. Felix, H. Fischmeister, L. Habraken, Y. Linblom, and M.O. Speidel (London, 1978) p.109.
18 P. Felix, Applied Science, eds. A.B. Hart and A.J.B. Cutler (London, 1972) p.331.
19 D.B. Lee and S.W. Woo, Intermetallics 13 (2005) 169.
20 D.B. Lee, M.H. Kim, and Y.C. Lee, Surface and Coatings Technology141 (2001) 232.9

[1]	Shilu ZHAO, Jun ZHANG, Changsheng LIU. Oxidation behavior of TiAlZrCr/(Ti,Al, Zr, Cr)N gradient films deposited by multi-arc ion plating [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(6): 473-480.
[2]	Y. H. Li; M. Krzyzanowski; J. H. Beynon and C. M. Sellars IMMPETUS( Institute for Microstructural and Mechanical Process Engineering: The University of Sheffield, Sheffield SI 3JD, UK). PHYSICAL SIMULATION OF INTERFACIAL CONDITIONS IN HOT FORMING OF STEELS [J]. Acta Metallurgica Sinica (English Letters), 2000, 13(1): 359-368.
[3]	DONG Zhili;MA Jusheng;TANG Xiangyun;YOU Liang Tsinghua University,Beijing,China lecturer Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China. HIGH TEMPERATURE OXIDATION AND STRUCTURE OF SCALE AND WHISKERS FOR Fe-Ni-Cr SEALING ALLOYS [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(8): 147-150.
[4]	LI Tiefan;LI Meishuan Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica Shenyang.China. DEFLECTION METHOD FROM TWO SIDES OXIDATION TO STUDY EFFECT OF Y ON INTERNAL STRESS OF OXIDE SCALES [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(12): 447-450.

High Temperature Oxidation of FGH96 P/M Superalloy

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 4

Recommended Articles

Metrics

Comments