Abstract: The microstructures of the Zn-27Al alloy after modification, solid-solution treatment, and natural aging were studied. It was clarified why the damping properties of Zn-27Al alloys, after treatment, had advanced most on the basis of analyzing the microstructures. Approximate expressions have been educed, which can be used to quantificationally work out the damping of the Zn-27Al alloy on the basis of the micro interface sliding model. By comparing the testing damping properties of the foundry Zn-27Al alloys and the Zn-27Al alloys after modification, solid solution, and natural aging, it was shown that the expressions were rational.

Key words: modification, solid solution and aging, damping micromechanism,