FORMATION OF SILICONIZED LAYER ON TiAI-BASED ALLOY AND THE OXIDATION RESISTANCE

Acta Metallurgica Sinica (English Letters) ›› 2003, Vol. 16 ›› Issue (6): 466-472 .

• Research Articles • Previous Articles Next Articles

FORMATION OF SILICONIZED LAYER ON TiAI-BASED ALLOY AND THE OXIDATION RESISTANCE

W.Liang[1], X.X.Ma[1], X.G.Zhao[1], J.Zhang[2], D.X.Zou[2]

[1]SchoolofMaterialsScienceandEngineering,TaiyuanUniversityofTechnology,Taiyuan030024,China [2]CentralIron＆SteelResearchInstitute,Beijing100081,China

Received:2002-11-07 Revised:2003-02-28 Online:2003-12-25 Published:2009-10-10
Contact: W.Liang

Abstract

Abstract: The Ti-48Al alloy was pack siliconized with 15i+85Al2O3. The microstructure of the siliconized coating on the TiAl-based alloy was analyzed and its effect on oxidation resistance was investigated. The specimens before and after cycle oxidation were examined by XRD and SEM equipped with XEDS. The results showed that the coating is composed of a thin Al2O3 outer layer and a composite inner layer of Ti5Si3 with an appropriate amount of Al2O3 dispersed in. Cycle oxidation tests showed that the high temperature oxidation resistance of TiAl-based alloy was greatly improved by forming such composite coating. No spallation and crack happened and the weight gain was very small after cycle oxidation at 900℃ for 314h.

Key words: TiAl-based alloy, microstructure, composite coating,

W.Liang, X.X.Ma, X.G.Zhao, J.Zhang, D.X.Zou. FORMATION OF SILICONIZED LAYER ON TiAI-BASED ALLOY AND THE OXIDATION RESISTANCE[J]. Acta Metallurgica Sinica (English Letters), 2003, 16(6): 466-472 .

References

1 S. Taniguchi, Materials and Corrosion 48(1997) 1．
2 G. Meier, Materials and Corrosion 47(1996) 595．
3 A. Rahmel, W. Quadakkers and M. Schutze, Materials and Corrosion 46(1995) 271．
4 K. Chan and Y.W. Kim, Metallurgical Transactions A24(1993) 113．
5 H.L. Qu, L. Zhou, H.R. Wei and Y.Q. Zhao, Materials Review 14 (2000) 32．
6 Y. Shida and H. Anada, Oxid. Met. 45 (1996) 197．
7 S. Taniguchi, T. Shibata and A. Murakami, Oxid. Met. 41(1994) 103．
8 M. Yoshihara, T. Suzuki and R. Tanaka, ISIJ Int. 31(1991) 1201．
9 S.C. Kung, Oxid. Met. 34 (1990) 217．
10 D. Xu, Z.H. Zheng, X.H. Liu, S.C. Zou, S. Taniquchi, T. Shibata and T. Yamada, Surf. Coat. Technol.66(1994) 486．
11 S. Taniguchi, T. Shibata, N. Asanuma, H. Lou, F. Wang and W. Wu, Oxid. Met. 39(1993) 457．
12 S. Taniguchi, T.Shibata and K. Takeuchi, Mater. Trans. JIM 32(1991) 299．
13 S.C. Huang, Metall. Trans. A22(1991) 427．
14 S.C.Huang, Metall. Trans. A22(1991) 2619．
15 K. Hashimoto, H. Doi, K. Kasahara, O. Nakano, T. Tsujimoto and T. Suzuki, J. Japan Inst. Metals52(1988) 1159．
16 Z.G. Liu, G. Frommeyer and M. Kreuss, Scripta Metall. 25(1991) 120．
17 H.E. Devee, A.G. Evans, G. R. Odette, R. Mehrabian, M.L. Emiliani and R.J. Hecht, Acta Metall. 38(1990) 1491．
18 S. Taniguchi, T. Kuwayama, Y.C. Zhu, Y. Matsumoto and T. Shibata, Materials Science and Engineering A277(2000) 229．
19 U. Hornauer, R. Gnzel, H. Reuther, E. Richter, E. Wieser, W. Mller, G. Schumacher, F. Dettenwanger and M. Schütze, Surf. Coating Technol. 125 (2000) 89．
20 H.N. Lee, Z.M. Park, M.H. Oh, K.Y. Kim and D.M. Wee, Scripta Mater. 41(1999) 1073．
21 Z.L. Tang, F.H. Wang and W.T. Wu, Materials Science and Engineering A276(2000) 70．
22 W. Liang and X.G. Zhao, Scripta Mater. 44 (2001) 1049．
23 C.G. Zhou, H.B. Xu, S.K. Gong and K.Y. Kim, Materials Science and Engineering A341(2003) 169．
24 H.G. Jung, D.J. Jung and K.Y. Kim, Surf. Coating Technol. 154(2002) 75．

FORMATION OF SILICONIZED LAYER ON TiAI-BASED ALLOY AND THE OXIDATION RESISTANCE

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 0

Recommended Articles

Metrics

Comments