PREPARATION OF Fe/Ni MULTILAYER FILMS AND THEIR MAGNETIC PROPERTIES

Abstract

Abstract: FeNi multilayer films were prepared by EB-PVD technique. A modified TG-DSCapparatus was used to measure their Curie temperatures, which were around 760°C,lower than that of pure Fe thin films. The easy magnetization axis was in-plane. Hightemperature annealing in vacuum decreased the coercivity sharply. The saturationmagnetization also changed with heat treatment. After annealing at the temperatureequal to the substrate temperature during deposition, the saturation magnetizationdecreased.

Key words: multilayer film, EB-PVD, Curie transitiou point, saturationmagnetization, coercivity

L.L. Liu, X.F. Bi, S.K. Gong. PREPARATION OF Fe/Ni MULTILAYER FILMS AND THEIR MAGNETIC PROPERTIES[J]. Acta Metallurgica Sinica (English Letters), 2002, 15(2): 182-186 .

[1]	H. Y. Liu, G. Wang, Y. Hong, D. C. Zeng. Effect of Heat Treatment Time on Dy-Cu Alloy Diffusion Process in Dy-Containing Commercial Nd-Fe-B Sintered Magnets [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(5): 496-502.
[2]	Md Anisur Rahman,Yun-Zhuo Lu,Qiang Luo,Shou-Jiang Qu,Feng-Xia Ye,Yi-Xuan Wu,Jun Shen. Comparative Study of the Magnetic Properties and Glass-Forming Ability of Fe-Based Bulk Metallic Glass with Minor Mn, Co, Ni, and Cu Additions [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(9): 834-839.
[3]	G.H. Dushaq, S.H.Mahmood, I. Bsoul, H.K. Juwhari, B.Lahlouh, M.A. AlDamen. Effects of Molybdenum Concentration and Valence State on the Structural and Magnetic Properties of BaFe_11.6Mo_xZn_0.4-xO₁₉ Hexaferrites [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(5): 509-516.
[4]	Kaifeng DONG,Xiaofei YANG,Junbing YAN,Weiming CHENG,Xiaomin CHENG. The effect of multilayer structure on magnetic properties of FePt thin films [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(1): 22-26.
[5]	J.Q. Zhou , M.G. Zhang. THE EFFECT OF Mo ADDITION ON COERCIVITY OF NdFeB SINTERED MAGNET PREPARED BY BLENDING METHOD [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(4): 557-560 .
[6]	D.B.Zhang, S.K.Gong, H.B.Xu. THE INFLUENCE OF Mo DIFFUSION ON THE THERMAL BEHAVIOR OF TBCs ON Ni3Al BASED ALLOY IC-6 [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(1): 45-48 .
[7]	H.B. Guo. FEM ANALYSIS OF THERMAL STRESSES IN GRADIENT THERMAL BARRIER COATINGS PRODUCED BY EB-PVD [J]. Acta Metallurgica Sinica (English Letters), 2001, 14(6): 493-496 .
[8]	S.K.Gong;L. Deng;F.S.Liu and H.B.Xu(Department of Material Science and Engineering,Beijing University of Aeronautics and Astronautics,Beijing 100083,China Manuscript received 26 August 1996). INVESTIGATIONS ON THE FORMATION OF INITIAL CRACKS IN THERMAL BARRIER COATINGS PREPARED BY EB-PVD [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(6): 519-522.
[9]	GAO Ruwei, XIAO MingshanShandong University, Jinan, ChinaZHOU Shouzeng, LIFubiao, ZHANG LidongNational Laboratory, University of Science and Technology Beijing, China Manuscript received 11 April, 1994. DEPENDENCE OF MAGNETISM OF Nd-Fe-B SINTERMAGNETS ON ORIENTATION MAGNETIC FIELD [J]. Acta Metallurgica Sinica (English Letters), 1994, 7(2): 100-102.
[10]	ZHANG Shaoying, TAI Lichi, CUI LiyaCentral Iron and Steel Research Institute, Beijing, China. STUDY OF STRUCTURE, MAGNETIC PROPERTIES AND PREPARATION OF Sm_2Fe_(17)N_x POWDER WITH HIGH ENERGY PRODUCTS [J]. Acta Metallurgica Sinica (English Letters), 1994, 7(1): 19-22.
[11]	XIAO Yaofu ZHANG Zhengyi TANG Weizhong University of Science and Technology Beijing,Beijing,China Associate Professor,University of Science and Technology Beijing,Beijing 100083,China. A NOVEL ROUTE FOR MAKING COERCIVE NdFeB POWDER——HDD PROCESS [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(7): 76-79.
[12]	CHEN Zhongmin XIE Faqin SHI Zhengxing WANG Leyi FU Hengzhi Northwestern Polytechnical University,Xi'an,China. COERCIVITY AND ITS GRAIN SIZE DEPENDENCE IN CAST-HOT PRESSED Pr-Fe-B MAGNETS [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(8): 128-132.
[13]	ZHANG Yanzhong;NIAN Suzhen Shanghai Iron and Steel Research Institute. THREE NEW Fe-BASED MICROCRYSTALLINE ALLOYS WITH SUPERIOR MAGNETIC PROPERTIES [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(12): 502-511.
[14]	ZHOU Shouzeng ZHANG Jin MA Deqing GAO Maolin University of Science and Technology Beijing,Beijing,China. MICROSTRUCTURE AND MAGNETIC HARDENING OF SINTERED NdFeB MAGNETS DOPPED WIHT Dy OR Dy_2O_3 [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(11): 351-356.
[15]	ZHOU Shouzeng TANG Weizhong WANG Run University of Science and Technology Beijing,Beijing,China. BOUNDARY MICROSTRUCTURE AND MAGNETIC HARDENING OF SINTERED NdFeB MAGNET [J]. Acta Metallurgica Sinica (English Letters), 1991, 4(7): 59-63.

PREPARATION OF Fe/Ni MULTILAYER FILMS AND THEIR MAGNETIC PROPERTIES

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments