DISTRIBUTION OF Ce AND S IN Fe-C-Si ALLOY AND THEIR INFLUENCE ON MORPHOLOGY OF GRAPHITE

Abstract

Abstract: Electrolytic extraction-radiometry and microradioautography techniques were used to study the distribution of nodulizing element Ce and anti-nodulizing element S in phases of high purity Fe-C-Si alloy.The results show that,besides forming inclusions,most of Ce atoms concentrate in graphite firstly.As the Ce content increases,the concentration of Ce in graphite tends to saturate,relatively large amount of Ce dissolves in the alloy.Usually,the sulphur also concentrates in graphite.However,it may exist in the form of FeS at the eutectic colony boundaries,if the concentration of S is at a quite high level.Very little amount of S dissolves in the alloy.The morphology of graphite depends upon the degree of saturation of Ce.It appears as nodular when Ce was saturated and,as vermicular while it was semi-saturated.

Key words: Ce.S.Fe-C-Si alloy, graphite

DU Weixi HAN Qiyong JIANG Qing ZHANG Zhongzhi ZHONG Weizhen LIU Shaoshou Jilin University of Technology,Changchun,China [Originally published in ACTA METALL SIN (CHINESE EDN) 24(5) 1988pp B313—B319,received 17 Octorber 1986;in revised form 3 April 19871 Beijing University of Science and Technology. DISTRIBUTION OF Ce AND S IN Fe-C-Si ALLOY AND THEIR INFLUENCE ON MORPHOLOGY OF GRAPHITE[J]. Acta Metallurgica Sinica (English Letters), 1989, 2(8): 87-93.

[1]	Sheng Cao, He-Jun Li, Ke-Zhi Li, Jin-Hua Lu, Lei-Lei Zhang. In Vitro Biocompatibility of MC3T3-E1 Osteoblast-like Cells on Arg-Gly-Asp Acid Peptides Immobilized Graphite-like Carbon Coating on Carbon/Carbon Composites [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(6): 558-566.
[2]	Shu LI, Yi FENG, Xiting YANG. Influence of adding carbon nanotubes and graphite to Ag-MoS₂ composites on the electrical sliding wear properties [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(1): 27-34.
[3]	Y.Z. Lan, S. Zhang, G.Y. Wu. A NEW PROCESS FOR PRODUCING HIGH GRADE GRAPHITE FOR USE IN MANUFACTURING Mg-C BRICKS IN [J]. Acta Metallurgica Sinica (English Letters), 2006, 19(2): 139-143 .
[4]	F.Lu, Q.P.Zhong. GALVANIC CORROSION AND PROTECTION OF GECM／LY12CZ COUPLES UNDER DIFFERENT ATMOSPHERIC EXPOSURE CONDITIONS [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(1): 41-45 .
[5]	L.X.Ding and Y.M.Wang Department of material, School of Mechanical Engineering, Shenyang University, Shenyang 110044, China. STUDY ON NODULE RATIO AND COMPACTED GRAPHITE RATIO OF IRON FLUID TREATED BY RARE EARTH MAGNESIUM ALLOY QUICKLY EXAMINED BY CONCENTRATED DIFFERENCE FIXING OXYGEN [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 907-910.
[6]	F.Lu;W.Y.Shen;J.G. Li and W.D. Zhen(Beijing Institute of Aeronautical Materials,Beijing 100095,China Manuscript received 26 August 1996). GALVANIC CORROSION BETWEEN GRAPHITE EPOXY COMPOSITE MATERIALS AND LY12CZ ALUMINUM ALLOY [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(6): 669-673.
[7]	WANG Chengfu, YING Meifang, FENG Yi, ZHANG XiaogunHefei University of Technology. Hefei, China. PHYSICAL PROPERTIES OF SHORT CARBON FIBRE REINFORCED SILVER COMPOSITES [J]. Acta Metallurgica Sinica (English Letters), 1994, 7(3): 157-160.
[8]	ZHAI Qijie;HU Hanqi University of Science and Technology Beijing,Beijing,China Faculty of Foundry,University of Science and Technology Beijing,Beijing 100083,China. EFFECT OF NITROGEN ON GRAPHITE MORPHOLOGY IN GRAY CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(8): 151-155.
[9]	ZHU Ruihui WANG Yu HAN Qiyong SONG Weixi University of Science and Technology Beijing,Beijing,China Engineer,Institute of Precise and Special New Materials,University of Science and Technology Beijing,Beijing 100083,China. DISTRIBUTION AND EFFECT OF Ce IN RE BEARING DUCTILE IRON [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(6): 419-424.
[10]	LIU Yongkun Southwestern Institute of Technology and Engineering,Chongqing,ChinaYANG Shihao Shandong Polytechnical University,Jinan,China. GROWTH MODE AND MODIFICATION OF GRAPHITE IN CAST IRON MELT [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(10): 263-267.
[11]	WANG Yanan Anshan Institute of Iron and Steel Technology,Anshan,ChinaSONG Weixi University of Science and Technology Beijing,Beijing,China WANG Yanan,Laboratory of Metallography,Anshan Institute of Iron and Steel Technology,Anshan,Liaoning 114002,China. MICROSTRUCTURE OF VERMICULAR GRAPHITE IN CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1990, 3(11): 357-359.
[12]	QIN Ziqiang YU Zongsen University of Science and Technology Beijing,Beijing,China QIN Ziqiang Department of Metal Physics,University of Science and Technology Beijing,Beijing,China. DYNAMIC SEGREGATION OF SULPHUR IN CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1989, 2(9): 202-204.
[13]	ZHOU Jiyang Dalian University of Technology,Liaoning,ChinaW.SCHMITZ S.ENGLER Aachen Institute of Technology,FRG Associate Professor,Divisionof Foundry,Dalian Institute of Technology,Liaoning,China. FORMATION OF AUSTENITE SHELL AROUND SPHEROIDAL GRAPHITE AND ITS EFFECT ON DETERIORATION OF GRAPHITE [J]. Acta Metallurgica Sinica (English Letters), 1989, 2(10): 261-265.
[14]	HAN Qiyong YANG Ping SONG Weixi University of Science and Technolonology Beijing,Beijing,China Division of Metallography,Dept.of Materials,University of Science and Technology Beijing,Beijing,China. DISTRIBUTION OF SULFUR IN HIGH TEMPERATURE PHASES OF CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1989, 2(10): 230-234.

DISTRIBUTION OF Ce AND S IN Fe-C-Si ALLOY AND THEIR INFLUENCE ON MORPHOLOGY OF GRAPHITE

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 14

Recommended Articles

Metrics

Comments