GROWTH MODE AND MODIFICATION OF GRAPHITE IN CAST IRON MELT

Abstract

Abstract: Using liquid quenching technique,the change of growth mode of graphite in cast iron melt was analysed.Based on the interface structure theory of crystal growth,the concept of multiplication of spiral growth steps was advanced and two basic multiplication models were given.It was proposed that multiplication of spiral steps is responsible for the change of growth mode of graphite in cast iron melt.The modifying elements such as Ce promote multiplication of spiral steps,which is regarded as the core of modification.Origination of screw dislocation and branch of the sector blocks in radius direction,both of which are essential to spheroidization of graphite in the melt,are caused by multiplication of spiral steps:and so is thickening of graphite plates.

Key words: graphite, crystallization morphology, growth mode, spiral growth seeps, cast iron

LIU Yongkun Southwestern Institute of Technology and Engineering,Chongqing,ChinaYANG Shihao Shandong Polytechnical University,Jinan,China. GROWTH MODE AND MODIFICATION OF GRAPHITE IN CAST IRON MELT[J]. Acta Metallurgica Sinica (English Letters), 1992, 5(10): 263-267.

[1]	Sheng Cao, He-Jun Li, Ke-Zhi Li, Jin-Hua Lu, Lei-Lei Zhang. In Vitro Biocompatibility of MC3T3-E1 Osteoblast-like Cells on Arg-Gly-Asp Acid Peptides Immobilized Graphite-like Carbon Coating on Carbon/Carbon Composites [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(6): 558-566.
[2]	Shu LI, Yi FENG, Xiting YANG. Influence of adding carbon nanotubes and graphite to Ag-MoS₂ composites on the electrical sliding wear properties [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(1): 27-34.
[3]	Weizhen OUYANG,Xia CAO2,Ning WANG. A mathematical model for electrochemical chloride removal from marine cast iron artifacts [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(2): 91-99.
[4]	Y.Z. Lan, S. Zhang, G.Y. Wu. A NEW PROCESS FOR PRODUCING HIGH GRADE GRAPHITE FOR USE IN MANUFACTURING Mg-C BRICKS IN [J]. Acta Metallurgica Sinica (English Letters), 2006, 19(2): 139-143 .
[5]	W.M. Mao, A.M. Zhao , X.Y. Zhong. SPHERICAL MICROSTRUCTURE FORMATION OF THE SEMI-SOLID HIGH CHROMIUM CAST IRON Cr20Mo2 [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(1): 77-82 .
[6]	F.Lu, Q.P.Zhong. GALVANIC CORROSION AND PROTECTION OF GECM／LY12CZ COUPLES UNDER DIFFERENT ATMOSPHERIC EXPOSURE CONDITIONS [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(1): 41-45 .
[7]	L.X.Ding and Y.M.Wang Department of material, School of Mechanical Engineering, Shenyang University, Shenyang 110044, China. STUDY ON NODULE RATIO AND COMPACTED GRAPHITE RATIO OF IRON FLUID TREATED BY RARE EARTH MAGNESIUM ALLOY QUICKLY EXAMINED BY CONCENTRATED DIFFERENCE FIXING OXYGEN [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 907-910.
[8]	Y.H. Qi, Y.Q. Ma, Z.P. Zhang and Z.K. Hei Institute of Materials & Technology, Dalian Maritime University, Dalian 116026, China. THE CORROSION OF Al CAST IRON IN Zn LIQUID BATH [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 940-945.
[9]	S.J. Chu; H.H. Lou and Q. Niu (College of Metallurgy, University of Science and Technology Beijing, Beijing 100083, China). MAKING DUCTILE CAST IRON WITH ESR PROCESS [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(3): 169-174.
[10]	Z.K. Fan;Y.Q. Wang;S.H. Liangand HS. Huang(School of Materials Science and Engineering, Xi'an University of Technology, Xi'an 710048, China)(Mechanical Engineering Department, Tsinghua University, Beijing 100084, China). STRENGTHENING CAST IRON MATRIX BY ALLOYING ELEMENTS WITH POSITIVE AND NEGATIVE SEGREGATION [J]. Acta Metallurgica Sinica (English Letters), 1997, 10(4): 329-332.
[11]	F.Lu;W.Y.Shen;J.G. Li and W.D. Zhen(Beijing Institute of Aeronautical Materials,Beijing 100095,China Manuscript received 26 August 1996). GALVANIC CORROSION BETWEEN GRAPHITE EPOXY COMPOSITE MATERIALS AND LY12CZ ALUMINUM ALLOY [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(6): 669-673.
[12]	WANG Chengfu, YING Meifang, FENG Yi, ZHANG XiaogunHefei University of Technology. Hefei, China. PHYSICAL PROPERTIES OF SHORT CARBON FIBRE REINFORCED SILVER COMPOSITES [J]. Acta Metallurgica Sinica (English Letters), 1994, 7(3): 157-160.
[13]	WANG Yu;SONG Weixi;HAN Qiyong University of Science and Technology Beijing,Beijing,China The Institute of Precise and Special New Materials, University of Science and Technology Beijing,Beijing 100083,China. SIZE DISTRIBUTION AND BEHAVIOUR OF VC PARTICLES IN FERRITIC NODULAR CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(8): 92-97.
[14]	ZHAI Qijie;HU Hanqi University of Science and Technology Beijing,Beijing,China Faculty of Foundry,University of Science and Technology Beijing,Beijing 100083,China. EFFECT OF NITROGEN ON GRAPHITE MORPHOLOGY IN GRAY CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(8): 151-155.
[15]	ZHAI Qijie HU Hanqi University of Science and Technology Beijing,China associate professor,Faculty of Foundry,University of Science and Technology Beijing,Beijing 100083,China. EFFECT OF NITROGEN ON MATRIX STRUCTURE OF GRAY CAST IRON [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(6): 370-372.

GROWTH MODE AND MODIFICATION OF GRAPHITE IN CAST IRON MELT

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments