Abstract: Fatigue crack propagation rate,da/dN,and threshold stress intensity range,ΔK_(th),of steel 20CrMnMo containing low carbon martensite or low carbon martensite/bainite(LCM/B) duplex structure,obtained by oil quenching and austempered at 360℃,have been measured using specimens under four-point bending.Observation was also made of the crack path and fracture morphology with relation to microstructure.The formation of LCM/B duplex structure,which caused by 20% lower bainite after short-time isothermal treatment,may re- markably increase ΔK_(th)and considerably decrease da/dN.The effect of microstructure on da/dN and ΔK_(th)was discussed with the emphasis on the crack propagation path.

Key words: low carbon martensite, duplex structure, fatigue crack propagation rate, threshold stress intensity range, crack path