Abstract: The relations between the non-equilibrium segregation process of P and the change of the texture in Fe-P alloys have been studied by analytical electron microscope and orientation distribution function.It was shown that P segregated preferentialy on the{110}slip planes, the P segregation structures with repeating cycle a=1.582 nm form at 450℃.<001>// ND direction abated.<111>//ND direction heightened.And{111}<110>has a tendancy to transform into{111}<143>texture in recovering process.{111}<143>direction trans- forms into{111}<112>direction after recrystalizing.A model to describe the effects of non-equilibrium segregation structures of P on orientation change was proposed and em- ployed to interpret the experiment results.

Key words: Fe-P Alloy, lattice image, recovering process, non-equalibrium segregation structure