MIXED MODE SCC OF 18-8 STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION

Abstract

Abstract: A series of mixed mode tests were carried out on 18-8 stainless steel in boiling 42% MgCl_2 solution.The results show that for any K_Ⅱ/K_Ⅰ ratio,the SCC direction coin- cides well with the crack tip maximum normal stress plane,while the SCC resistance of the material reduces as the ratio of K_Ⅱ/K_Ⅰ increases.The experimental results were discussed in the light of anode dissolving mechanism and the effect of mixed mode loading on crack tip stress and strain.It is concluded that for fracture analysis if mixed mode cracks were simply taken into account as mode Ⅰ cracks,and only mode Ⅰ testing results as mode Ⅰ fracture criter- ion were employed,it may not be safe.

Key words: 18-8 stainless steel, stress corrosion, mixed mode

GAO Hua CAO Weijie ZHOU Deqi WANG Ruizhen Shanghai University of Engineering Science,Shanghai,China. MIXED MODE SCC OF 18-8 STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION[J]. Acta Metallurgica Sinica (English Letters), 1992, 5(8): 104-109.

[1]	Zhixiong Zhu, Xingxu Jiang, Gang Wei, Xiaogang Fang, Zhihong Zhong, Kuijing Song, Jian Han, Zhengyi Jiang. Influence of Zn Content on Microstructures, Mechanical Properties and Stress Corrosion Behavior of AA5083 Aluminum Alloy [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(10): 1369-1378.
[2]	Jin-Jin Zhao, Xian-Bin Liu, Shuai Hu, En-Hou Han. Effect of Cl^- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO₂ Environment [J]. Acta Metallurgica Sinica (English Letters), 2019, 32(12): 1459-1469.
[3]	Hong-Liang Ming,Zhi-Ming Zhang,Peng-Yuan Xiu,Jian-Qiu Wang,En-Hou Han,Wei Ke,Ming-Xing Su. Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(9): 848-858.
[4]	Jian Chen, Jian-Qiu Wang, En-Hou Han, Wei Ke, D. W. Shoesmith. Effect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(1): 1-7.
[5]	Zhiyong LIU, Cuiwei DU, Xin ZHANG, Fuming WANG,Xiaogang LI. Effect of pH Value on Stress Corrosion Cracking of X70 Pipeline Steel in Acidic Soil Environment [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(4): 489-496.
[6]	Y. Wang, J. Chen, H.B. Li. IMPROVED COHESIVE ZONE MODEL AND ITS APPLICATION IN INTERFACE CONTACT ANALYSIS [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(4): 295-302 .
[7]	J.X. Pan, K.Y. Kim. THE EFFECT OF W ON THE REPASSIVATION BEHAVIOR OF Ni-ADDED STAINLESS STEELS [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(4): 489-496 .
[8]	H.R. Dong , W.L. Guo. Mechanism Analysis of Thickness Effect on Mixed Mode I/II Fracture of LC4-CS Aluminum Alloy [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(3): 255-262 .
[9]	S.Q. Li; J.I. Dickson and J.P. Bailon (Central Iron and Steel Research Institute (CISRI), Beijing 100081, China)(Ecole Polytecnique de Montreal, Montreal H3C 3A7, Canada). STUDY ON FRACTOGRAPHY OF TRANSGRANULAR SCC OF 70Cu-3OZn IN AN AMMONIACAL SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(5): 347-357.
[10]	ZHANG Yue;CHU Wuyang;XIAO Jimei(Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China) OUYANG Shixi;YUAN Runzhang(State Key Laboratory for Synthesis and Processing of Advanced Materials.Wuhan University of Technology,Wuhan 430070,China). INTERPHASE STRESS CORROSION CRACKING OF ALLOY Ti-24Al-11Nb IN METHANOL SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(2): 121-128.
[11]	HUANG Yanliang CAO Chu'nan LIN Haichao LU Ming Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China Ph D student,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang 110015,China. SCC MECHANISM OF STAINLESS STEEL AISI 321 IN ACIDIC CHLORIDE SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1993, 6(12): 416-420.
[12]	QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing,Beijing,China. CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(9): 178-182.
[13]	LU Minxu LIU Xiaokun WANG Jianjun FU Xiangjiong ZHENG Xiulin Northwestern Polytechnical University,Xi'an,China Lecturer,Department No.4.Northwestern Polytechnical University,Xi'an 710072,China. EFFECTS OF HEAT TREATMENT AND ENVIRONMENT ON CRACK PROPAGATION RATE IN STEEL GC-4 UNDER CORROSION FATIGUE AND STRESS CORROSION [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(9): 183-189.
[14]	CHEN Liangshi;GAO Xuejie;FENG Tao;LIU Minzhi Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia,Sinica Shenyang,China. SCF FEATURE OF AUSTENITIC STAINLESS STEEL IN BOILING MgCl_2SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(12): 451-456.
[15]	LJ Benshun Harbin Institute of Technology,Harbin,China CHEN Xiangping lianghan Petroleum Institute,Wuhan,China. CORRELATION BETWEEN MICROSTRUCTURE AND STRESS CORROSION CRACKING SUSCEPTIBILITY OF 2091 ALLOY [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(12): 483-488.

MIXED MODE SCC OF 18-8 STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments