Abstract: The oxidation behaviour of high Cr Cast iron was investigated at 950 and 800℃ in terms of Cr content in matrix and the amount of carbide.The morphology and types of oxide films and the microstructure of subsurface were also examined.The main conclusions are:1)The original chromium content in the matrix determines the type of oxide film and it is an important factor for the oxidation resistance of high chromium cast iron;2) The oxidation resistance improves with increasing carbide content at 950℃ because of the decomposition of the carbide,while the decompsition of the carbide do not take place at 800℃ so the oxidation resisteance do not improve with increasing carbide volume.

Key words: high chromium cast iron, oxidation resistance, carbide