Acta Metallurgica Sinica (English Letters) ›› 1993, Vol. 6 ›› Issue (12): 459-464.

• Research paper • Previous Articles     Next Articles

INFLUENCE OF APPLIED POTENTIAL AND LOADING WAVEFORM ON FATIGUE CRACK GROWTH FOR STEEL A537 IN 3.5% NaCl SOLUTION

LI Jin WANG Zengfu KE Wei Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang 110015,China   

  • Received:1993-12-11 Revised:1993-12-11 Online:1993-12-11 Published:2009-10-10

Abstract: Influence of applied potentials and loading waveform on the fatigue crack growth for steel A537 in 3.5% NaCl solution,and corresponding straining electrode behaviour have been studied.Under the applied potentials over or below -800mV(SCE),the anodic dissolution or the hydrogen embrittlement is predominatant,respectively.For applied anodic potential,the acceleration effect of continuous loading pattern on the CF crack growth mainly appeared at the range of low ΔK values,while for cathodic potential,it appeared at the high ΔK values.The continuous straining causes a decrease of natural potential and an increase of anodic dissolution current.

Key words: corrosion fatigue, steel A537, waveform, potential, straining eleclrode