PREPARATION AND SOLIDIFICATION CHARACTERISTIC OF IN SITU DIRECTIONALLY SOLIDIFIED EUTECTIC Al_(11)La_3/Al COMPOSITE

Acta Metallurgica Sinica (English Letters) ›› 1993, Vol. 6 ›› Issue (5): 278-282.

• Research paper • Previous Articles Next Articles

PREPARATION AND SOLIDIFICATION CHARACTERISTIC OF IN SITU DIRECTIONALLY SOLIDIFIED EUTECTIC Al_(11)La_3/Al COMPOSITE

Received:1993-10-25 Revised:1993-10-25 Online:1993-10-25 Published:2009-10-10

Abstract

Abstract: In situ eutectic Al_(11)La_3/Al composite material with regular arrangement was prepared by zone melt liquid metal cooling directionally solidification under conditions of high temperature gradient G=700K/cm and growth rate R=6.0-20.0μm/s.Superpose diffraction pat- tern of Al_(11)La_3/Al composite shows that the preferred growth direction is[100]Al// [33]Al_(11)La_3,and the habit plane is(002)Al//(116)Al_(11)La_3.A low density(103)twin is ob- served in Al_(11)La_3 and the growth of(103)twin induces to branching to change the interlamellar spacing.

Key words: eutectic solidification, directional solidification, AI+(La, Al)

DONG Hongbiao JI Yongyi ZHU Jun LU Shuzu ZHONG Xueyou University of Science and Technology,Beijing,ChinaLI Jianguo Northwestern Polytechnical University,Xi'an,China DONG Hongbiao,lecturer,Department of Metallurgy,University of Science and Technology Beijing,Beijing 100083,China. PREPARATION AND SOLIDIFICATION CHARACTERISTIC OF IN SITU DIRECTIONALLY SOLIDIFIED EUTECTIC Al_(11)La_3/Al COMPOSITE[J]. Acta Metallurgica Sinica (English Letters), 1993, 6(5): 278-282.

[1]	Yue-Ling Guo, Li-Na Jia, Hua-Rui Zhang, Bin Kong, Yong-Lin Huang, Hu Zhang. Microstructure and High-Temperature Oxidation Behavior of Dy-Doped Nb-Si-Based Alloys [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(7): 742-752.
[2]	Si-Yu Sun, Qiao-Dan Hu, Wen-Quan Lu, Zong-Ye Ding, Ming-Qin Xu, Ming-Xu Xia, Jian-Guo Li. In situ Study on the Growth Behavior of Primary Al₃Ni Phase in Solidifying Al-Ni Alloy by Synchrotron Radiography [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(6): 668-672.
[3]	Hong-Min Jia, Xiao-Hui Feng, Yuan-Sheng Yang. Microstructure Evolution and Growth Orientation of Directionally Solidified Mg-4 wt% Zn Alloy with Different Growth Rates [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(12): 1185-1191.
[4]	Gong-Sheng Song, Shuo Sun, Zhong-Chi Wang, Cheng-Zhi Luo, Chun-Xu Pan. Synthesis and Characterization of Electroless Ni-P/Ni-Mo-P Duplex Coating with Different Thickness Combinations [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(10): 1008-1016.
[5]	Shu Chen, Jiu-Zhou Zhao, Hong-Xiang Jiang, Jie He. Microstructure Evolution of a Ternary Monotectic Alloy During Directional Solidification [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(3): 316-321.
[6]	Shaojun Liu, Guangyu Yang, Wanqi Jie. Microstructure, Microsegregation, and Mechanical Properties of Directional Solidified Mg-3.0Nd-1.5Gd Alloy [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(6): 1134-1143.
[7]	Wang Lingshui, Shen Jun, Xiong Yilong, Du Yujun, Fu Hengzhi. Phase and Microstructure Selection During Directional Solidification of Peritectic Alloy Under Convection Condition [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(4): 585-592.
[8]	Jianbo YU,Zhongming REN,Weili REN,Kang DENG,Yunbo ZHONG. Solidification structure of eutectic Al-Si alloy under a high magnetic field-aid-electromagnetic vibration [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(3): 191-196.
[9]	Jianbo YU,Zhongming REN,Weili REN,Kang DENG,Yunbo ZHONG. Effects of electromagnetic vibration on the structure and mechanical properties of Al-6%Si alloy during directional solidification [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(1): 35-39.
[10]	Z.M. Zhang, T. Lu, C.J. Xu, X.F. Guo. MICROSTRUCTURE OF BINARY Mg-Al EUTECTIC ALLOY WIRES PRODUCED BY THE OHNO CONTINUOUS CASTING PROCESS [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(4): 275-281 .
[11]	D.H.Kim. EFFECT OF CARBON AND BORON ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A SINGLE CRYSTAL SUPERALLOY RR 2072 [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(1): 33-38 .
[12]	F.S.Liu, J.L.Xu, C.G.Zhou, S.K.Gong, H.B.Xu. Si-Al COATING ON PURE MOLYBDENUM SUBSTRATE AND ITS CYCLIC OXIDATION BEHAVIOR [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(5): 672-676 .
[13]	J.L. Xu, F.S. Liu, C.G. Zhou. CODEPOSITION OF ALUMINUM AND SILICON ON PURE MOLYBDENUM SUBSTRATE USING HALIDE ACTIVATED PACK CEMENTATION TREATMENTS [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(2): 167-171 .
[14]	J. Feng,W.D. Huang,X. Lin,T. Li,Y.F. Xue and Y.H. Zhou(State Key Lab. of Solidilication Processing, Northwestern Polytechnical University, Xi'an 710072, China). CELLULAR SPACING SELECTION OF Al-0.53wt%Zn ALLOY UNDER NEAR-RAPID DIRECTIONAL SOLIDIFICATION CONDITION [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(5): 320-324.
[15]	W. H. JIANG; X.D. YAO; H.R. GUAN; and Z. Q. HU(Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110015, China)(Shenyang Polytechnic University, Shenyang 110023, China). HIGH TEMPERATURE FATIGUE BEHAVIOUR OF A DIRECTIONALLY SOLIDIFIED COBALT-BASE SUPERALLOY [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(2): 111-115.

PREPARATION AND SOLIDIFICATION CHARACTERISTIC OF IN SITU DIRECTIONALLY SOLIDIFIED EUTECTIC Al_(11)La_3/Al COMPOSITE

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments