FATIGUE BEHAVIOUR OF M/B DUPLEX STRUCTURE IN A HIGH CARBON Cr-Mo-W STEEL

Acta Metallurgica Sinica (English Letters) ›› 1993, Vol. 6 ›› Issue (5): 316-319.

• Research paper • Previous Articles Next Articles

FATIGUE BEHAVIOUR OF M/B DUPLEX STRUCTURE IN A HIGH CARBON Cr-Mo-W STEEL

Received:1993-10-25 Revised:1993-10-25 Online:1993-10-25 Published:2009-10-10

Abstract

Abstract: Determination was carried out of fatigue crack propagation rate of steel 65Cr5Mo3W2VSiTi (LM2)with various bainite contents and M/B duplex structure tempered at various tempera- tures.The threshold value of fatigue for each processing was estimated by experimental data. The mechanism for fatigue crack propagation of M/B duplex structure in steel LM2 seems to be non-continuous.The calculated fatigue crack micro-propagation rates are found to agree with the experimental data.

Key words: duplex structure, fatigue crack propagation rate, threshold value, steel 65Cr5Mo3W2VSiTi

TIAN Baohong ZHENG Shi'an WU Lei Luoyang Institute of Technology,Luoyang,China ZHENG Shi'an,associate professor,Department of Materials Engineering,Luoyang Institute of Technology,Luoyang 471039,China. FATIGUE BEHAVIOUR OF M/B DUPLEX STRUCTURE IN A HIGH CARBON Cr-Mo-W STEEL[J]. Acta Metallurgica Sinica (English Letters), 1993, 6(5): 316-319.

[1]	Tian LIANG, Xiaoqiang HU, Xiuhong KANG, Dianzhong LI. Microstructure Evolution of a Cold-rolled 25Cr-7Ni-3Mo-0.2N Duplex Stainless Steel during Two-step Aging Treatments [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(5): 517-522.
[2]	Jie SHI, Haifeng XU, Jie ZHAO, Wenquan CAO, Chang WANG, Cunyu WANG, Jian LI,Han DONG. Effect of austenization temperature on the microstructure evolution of the medium manganese steel (0.2C-5Mn) during ART-annealing [J]. Acta Metallurgica Sinica (English Letters), 2012, 25(2): 111-123.
[3]	ZHENG Yesha WANG Zhongguang AI Suhua State Key Laboratory of Fatigue and Fracture for Materials,Institute of Metal Research,Academia Sinica,Shenyang,110015,China. MICROFRACTOGRAPHY OF NEAR-THRESHOLD FATIGUE CRACK PROPAGATION IN DUAL-PHASE STEELS [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(5): 385-389.
[4]	LI Yongjun Xi′an Jiaotong University,Xi′an,China. FATIGUE FRACTURE BEHAVIOR OF LOW CARBON MARTENSITE AND MARTENSITE/BAINITE DUPLEX STRUCTURE IN STEEL 20CrMnMo [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(3): 212-217.

FATIGUE BEHAVIOUR OF M/B DUPLEX STRUCTURE IN A HIGH CARBON Cr-Mo-W STEEL

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 4

Recommended Articles

Metrics

Comments