EFFECTS OF STRESS RATIO AND FREQUENCY ON CORROSION FATIGUE CRACK GROWTH MECHANISM IN LOW ALLOY STEELS

Acta Metallurgica Sinica (English Letters) ›› 1993, Vol. 6 ›› Issue (6): 373-378.

• Research paper • Previous Articles Next Articles

EFFECTS OF STRESS RATIO AND FREQUENCY ON CORROSION FATIGUE CRACK GROWTH MECHANISM IN LOW ALLOY STEELS

Received:1993-12-25 Revised:1993-12-25 Online:1993-12-25 Published:2009-10-10

Abstract

Abstract: Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measured experimentally,and the PH and electrode potential within crack were also measured continuously along with crack propagating.It showed that the increase of crack growth rate,caused by both decreasing frequency and raising stress ratio,was mainly accelerated by hydrogen embrittlement.

Key words: corrosion fatigue, stress ratio, crack growth, electrode potential, steel ZG20SiMn, steel SM50B-Zc

HAN Enhou HAN KYumei ZHENG Yuli KE Wei Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China postdoctoral,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang 110015,China. EFFECTS OF STRESS RATIO AND FREQUENCY ON CORROSION FATIGUE CRACK GROWTH MECHANISM IN LOW ALLOY STEELS[J]. Acta Metallurgica Sinica (English Letters), 1993, 6(6): 373-378.

[1]	Jiaqi Hu, Qite Li, Hong Gao. Influence of Twinning Texture on the Corrosion Fatigue Behavior of Extruded Magnesium Alloys [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(1): 65-76.
[2]	Yan Liu, Jun Zhang, Shu-Jun Li, Wen-Tao Hou, Hao Wang, Qin-Si Xu, Yu-Lin Hao, Rui Yang. Effect of HIP Treatment on Fatigue Crack Growth Behavior of Ti-6Al-4V Alloy Fabricated by Electron Beam Melting [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(12): 1163-1168.
[3]	Zuo-Yan Ye, Dao-Xin Liu, Xiao-Hua Zhang, Xiao-Ming Zhang, Ming-Xia Lei, Zhi Yang. Corrosion Fatigue Behavior of 7A85 Aluminum Alloy Thick Plate in NaCl Solution [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(8): 1047-1054.
[4]	Ke Wang, Fang Wang, Wei-Cheng Cui, A.-Li Tian. Prediction of Cold Dwell-Fatigue Crack Growth of Titanium Alloys [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(5): 619-627.
[5]	Amir SULTAN, Riffat Asim PASHA,Mifrah ALI, Muhammad Zubair KHAN, Muhammad Afzal KHAN, Naeem Ullah DAR,Masood SHAH. Numerical Simulation and Experimental Veri?cation of CMOD in SENT Specimen: Application on FCGR of Welded Tool Steel [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(1): 92-96.
[6]	Jianping TAN, Guozhen WANG, Fuzhen XUAN and Shan-Tung TU. Creep crack growth in a Cr-Mo-V type steel: experimental observation and prediction [J]. Acta Metallurgica Sinica (English Letters), 2011, 24(2): 81-91.
[7]	Fang WANG,Weicheng CUI. Effect of three dimensional stress state on unstable fracture condition and crack opening level in a new crack growth model [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(1): 41-49.
[8]	Liangbi LI,Zhengquan WAN,Zili WANG,Chunyan JI. Residual stress relaxation in typical weld joints and its effect on fatigue and crack growth [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(3): 202-210.
[9]	J.X.Dong, M.C.Zhang, Y.P.Zeng, X.S.Xie. CREEP CRACK GROWTH BEHAVIOR OF ALLOY 718 DURING HIGH TEMPERATURE EXPOSURE [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(2): 164-172 .
[10]	X.B.Liu, L.Z.Ma, K.M.Chang, E.Barbero. FATIGUE CRACK PROPAGATION OF Ni-BASE SUPERALLOYS [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(1): 55-64 .
[11]	H.C.Yang. INVESTIGATION OF THE LOW-CYCLE FATIGUE AND FATIGUE CRACK GROWTH BEHAVIORS OF P91 BASE METAL AND WELD JOINTS [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(4): 597-600 .
[12]	F.Z.Shen. FAILURES AND THE LIFE OF FURNACE TUBES [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(4): 419-425 .
[13]	H.Q.Zhang. ON FATIGUE CRACK PATH DEVIATION AT ELEVATED TEMPERATURE IN ELECTRON BEAM REPAIRED WELDMENTS OF TURBINE DISK [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(4): 584-590 .
[14]	Q.J. Zhu, Y.H. Chen , J. Chen. Interfacial Debonding of FRC Under Cyclic Loading [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(3): 327-330 .
[15]	W.C.Cui, X.P.Huang. A GENERAL CONSTITUTIVE RELATION FOR FATIGUE CRACK GROWTH ANALYSIS OF METAL STRUCTURES [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(5): 342-354 .

EFFECTS OF STRESS RATIO AND FREQUENCY ON CORROSION FATIGUE CRACK GROWTH MECHANISM IN LOW ALLOY STEELS

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments