STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

Acta Metallurgica Sinica (English Letters) ›› 1996, Vol. 9 ›› Issue (3): 227-231.

• Research paper • Previous Articles Next Articles

STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

WU Zhixue ; LU Wenge and XU Hao1)(Fushun Petroleum institute, Fushun 113001, China)2)(State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, ChineseAcademy of Sciences, Shenyang 110015, China)3)(Institute of Mechanical Engineering, Northeastern University, Shenyang 110006, China)Manuscript received 19 July 1995, in revised form 11 April 1996

Received:1996-06-25 Revised:1996-06-25 Online:1996-06-25 Published:2009-10-10

Abstract

Abstract: Rotary bending fatigue tests were carried out for smooth specimens of a mediumcarbon steel with two different grain sizes near the fatigue limit. The process of fatigue damagewas observed by replication method, and the effects of grain size,stress level and microstructure on surface damage were studied. The effect of following cycle stress level on the coaxing effects was also discussed. The fatigue limit is the maximum stress at which the short fatigue crack initiates and becomes a non-propagating crack.. The length of non-propagating crack is related to grain sizes and stress level. The coaxing effects disappear when the following stress level is greater than the critical value.

Key words: fatigue damage, fatigue limit, coaxing effect

References

Related Articles 7

[1]	Shasha Zhang, Niels van Dijk, Sybrand van der Zwaag. A Review of Self-healing Metals: Fundamentals, Design Principles and Performance [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(9): 1167-1179.
[2]	Z.X.Wu, X.C.Wu. SHORT FATIGUE CRACK PARAMETER BASED ON THE TOTAL CRACK AREA [J]. Acta Metallurgica Sinica (English Letters), 2001, 14(4): 235-240 .
[3]	Z.X. Wu Engineering College, Yangzhou University, Yangzhou 225009, China. THE CHARACTERISTICS OF SHORT CRACKS AND EQUIVALENT PARAMETER OF FATIGUE DAMAGE [J]. Acta Metallurgica Sinica (English Letters), 2000, 13(4): 955-960.
[4]	WU Zhixue;XU Hao(Institute of Mechanical Engineering,Northeastern University,Shenyang 110006,China)(Fushun Petroleum institute,Fushun 113001.China).(State Key Laboratory for Fatigue and Fracture of Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110015,China) Manuscript received 2 July 1995. BEHAVIOUR OF INITIATION AND GROWTH OF SHORT FATIGUE CRACKS [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(1): 65-70.
[5]	KANG Zengqiao GAI Xiuying LI Jiabao WANG Zhongguang State Key Laboratory for Fatigue and Fracture of Materials Institute of Metal Research,Academia Sinica,Shenyang,China Research Assistant,Institute of Metal Research,Academia Sinica,Shenyang 110015,China. INFLUENCE OF RESIDUAL STRESS AND SURFACE MORPHOLOGY ON FATIGUE PROPERTIES OF STEEL 60Mn [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(6): 477-483.
[6]	TUNG Xiaoyan Northwestern Polytechnical University,Xi'an,ChinaWANG Dejun XU Hao Northeast University of Technology,Shenyang,China. HEAT ENERGY DISSIPATION IN FATIGUE DAMAGE PROCESS [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(5): 373-378.
[7]	WANG Hongwei MA Jinsheng NAN Junma HE Jiawen Xi′an Jiaotong University,Xi′an,China. SURFACE YIELD STRENGTH AND FATIGUE LIMIT FOR STEELS [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(2): 116-120.

STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 7

Recommended Articles

Metrics

Comments