Abstract: The oxidation behaviors of two kinds of low segregation Ht-Cr-Al based superalloys have been studied between 1000-1100℃, and compared with that of general Mt-Cr-Al based superalloys. The results indicated that the simultaneous additions of 0.1 wt% S and 0. 1 wt% Zr to low segregation alloys increase the oxidation rate of Al2O3-forming alloy and improve the scale adherence. The addition of 0.1 wt% Zr can ,minimize the negative effects of S on the adherence of Al2O3 scale. Low amounts of S(≤50 ppm wt) have no obviously negative effects on the adherence of Cr2O3 scale formed on one of the low segregation superalloys.

Key words: oxidation behavior, low segregation, Ni-Cr-Al based superalloy, trace elements, scale adherence