Abstract: The tensile properties of three different carbonfiberreinforced carbon composites (C/C), mat C/C, 2D laminate and 4D C/C, were investigated under the combined influence of temperature and loading rate. From the experiments the following could be concluded: loading rate between 10-1-10 mm/min was valid; the fracture stress of the three kinds of C/C composites increased with increasing temperature in the range from room temperature to 1900, and the initial modulus of 2D laminate C/C composites increased with the increase of temperature up to 2000.

Key words: tensile testing, C/C composite, high temperature, mechanical property