Abstract: Anovel silicon containing carbon precursor was synthesised by reacting a petroleum pitchfraction and polydimethylsilane. The precursor containing about 26wt% Si was meltspunintofibresand then oxidativelystabilised in airto renderthefibresinfusiblebefore pyrolysisat1200℃underinertatmospheretoproduceC Sialloy( CSA) fibres. Theextentofstabili sation wasfoundto becriticalto the development of mechanicalstrength of thefibres which varied with heattreatmenttemperature, showing a maximum at 1200 ℃when thestrength was 1 4 1 6 GPa. Thesestrengthsareremarkably goodconsideringthelow modulus whichis duetothe quite high failurestrains. Thefibrescanshow excellentresistanceto oxidation if given an initialshortexposureto oxygen athigh temperature duetotheformation of an im perceptiblelayer of silica. CSAfibreshavethe advantagesof both carbon fibresand SiCfi bres,thusextended application areascan beenvisaged .

Key words: carbon silicon alloy fibres, oxidation resistance, mechanicalproperty