PHASE STRUCTURE FACTOR AND INTERFACE CONJUNCTION FACTOR  OF CAST IRON AND ITS COMPOSITION DESIGN

Acta Metallurgica Sinica (English Letters) ›› 1999, Vol. 12 ›› Issue (4): 401-407.

• Research paper • Previous Articles Next Articles

PHASE STRUCTURE FACTOR AND INTERFACE CONJUNCTION FACTOR OF CAST IRON AND ITS COMPOSITION DESIGN

Z.L.Li,Z.L.Liu ,F.Y.Li,X.P.Yang and Z.G.Gu Departmentof Materials Science and Engineering ,Liaoning Institute of Technology,Jinzhou 121001 ,China

Received:1999-08-25 Revised:1999-08-25 Online:1999-08-25 Published:2009-10-10

Abstract

Abstract: Theempiricalelectrontheory of solidsand molecules( EET) and theimproved TFDtheory wereapplied tocalculatethe phasestructurefactorsand interfaceconjunction factorsofcom mon alloying elementsincastiron. Akind of Si- Mo- Cu ductileiron with rareearth Mg asnodularizer was designed accordingtothese valenceelectron structure parameters. Actual applicationtestsshow thatthelongevity of thisiron is 1.5 timesof thatof high manganesesteel. This accordance of theoretical results and actual effectsshows the composition design methodcan beused in othercastiron research.

Key words: phasestructure factor, interface conjunction factor, ductile iron, wear resistance, composition design

Z.L.Li,Z.L.Liu ,F.Y.Li,X.P.Yang and Z.G.Gu Departmentof Materials Science and Engineering ,Liaoning Institute of Technology,Jinzhou 121001 ,China. PHASE STRUCTURE FACTOR AND INTERFACE CONJUNCTION FACTOR OF CAST IRON AND ITS COMPOSITION DESIGN[J]. Acta Metallurgica Sinica (English Letters), 1999, 12(4): 401-407.

[1]	Cui Junjun, Zhang Hongyun, Chen Liqing, Li Haizhi, Tong Weiping. Microstructure and Mechanical Properties of a Wear-Resistant As-Cast Alloyed Bainite Ductile Iron [J]. Acta Metallurgica Sinica (English Letters), 2014, 27(3): 476-482.
[2]	G.W. Chang, H.X. Wang, X.D.Yue, H.L. Zhang. Research Of The Feeding Speed Adopting Cored-Wire Method To Spheroidize Ductile Iron Melt [J]. Acta Metallurgica Sinica (English Letters), 2008, 21(5): 362-368 .
[3]	Q.Z. Cai, B.K. Wei , Y. Tanaka. Fatigue Properties of Austempered Ductile Iron(ADI) in Water Environment [J]. Acta Metallurgica Sinica (English Letters), 2004, 17(2): 122-130 .
[4]	Y. P. Zhang;J.X. Zhu; Y. Q. Wang and J.Y.Su(Institute of Cast Iron Research, Xi'an University of Technology, Xi'an 710048, China)(Department of Mechanical Engineering, Xi'an Jiaotong University, Xi'an 710049, China). EFFECT OF SILICON ON PRODUCING DUCTILE IRON WITH COMPLEX STRUCTURE OF BAINITE AND MARTENSITE [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(1): 25-28.
[5]	L. P. Xu; M. H. Xu; L. Li; Y.A. Min; X.Z Xuand R.H .Liu (Department of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) (Shanghai No.5 Iron and Steel Factory, Shanghai 200940,China). COMPOSITION DESIGN FOR A BEARING STEEL WITH LIMITED HARDENABILITY [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(5): 379-382.
[6]	FA N Zhikang (Xi'an University of Technology, China)SMALLMANRE(University of Birmingham,UK Manuscript received 3 January 1995). CARBIDE FORMATION IN AUSTEMPERED DUCTILE IRON ALLOYED WITH NICKEL AND COPPER [J]. Acta Metallurgica Sinica (English Letters), 1995, 8(3): 190-194.
[7]	ZHOU Jiyang XIE Zuhua ZHONG Fenqi Dalian University of Technology,Dalian,China. EFFECT OF AUSTENITIC DENDRITES ON MECHANICAL PROPERTIES OF DUCTILE IRON [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(11): 375-377.

PHASE STRUCTURE FACTOR AND INTERFACE CONJUNCTION FACTOR OF CAST IRON AND ITS COMPOSITION DESIGN

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 7

Recommended Articles

Metrics

Comments