THE STUDY ON BEHAVIOR OF Al  2O  3  C BRICK FOR BLAST FURNACE  AT HIGH TEMPERATURE

Acta Metallurgica Sinica (English Letters) ›› 1999, Vol. 12 ›› Issue (5): 1106-1110.

• Research paper • Previous Articles Next Articles

THE STUDY ON BEHAVIOR OF Al 2O 3 C BRICK FOR BLAST FURNACE AT HIGH TEMPERATURE

W.H.Tong, F.M.Shen and W.Z.Wang The Department of Ferrous Metallurgy, Northeastern University, Shenyang 110006,China

Received:1999-10-25 Revised:1999-10-25 Online:1999-10-25 Published:2009-10-10

Abstract

Abstract: In experimental conditions simulating reducing atmosphere in Blast Furnace, the samples of Al 2O 3 C brick were heated at high temperature. Their microscopic structures were observed by Scanning Electric Telescope and rupture and compressive strength measured before and after heating observed the changes. According to these measurements, the reasons causing the changes were analyzed.

Key words: blast furnace, Al 2O 3 C brick, microscopic structure, rupture and compressive strength

W.H.Tong, F.M.Shen and W.Z.Wang The Department of Ferrous Metallurgy, Northeastern University, Shenyang 110006,China. THE STUDY ON BEHAVIOR OF Al 2O 3 C BRICK FOR BLAST FURNACE AT HIGH TEMPERATURE[J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 1106-1110.

References

Related Articles 5

[1]	Xuefeng YANG,Mansheng CHU,Fengman SHEN,Zhuming ZHANG. Mechanism of zinc damaging to blast furnace tuyere refractory [J]. Acta Metallurgica Sinica (English Letters), 2009, 22(6): 454-460.
[2]	C.J. Liu, M.F. Jiang, Y.S. Wang, J.J. Chen , C.L. Li. EFFECTS OF La ON STRUCTURE AND PROPERTIES OF HEAVY RAIL STEEL [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(6): 701-706 .
[3]	P.Y.Zong and L.R.Zhang Mechanical Engineering College, Shenyang University, Shenyang 110044, China. THE DEVELOPMENT OF COLD WELDING SURFACING ELECTRODE FOR BLAST FURNACE VALVE [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(5): 925-928.
[4]	DU Hegui; ZOU Anhua, Northeast University of Technology, Shenyang, China Du Hegui, Professor, Department of Ferrous Metallurgy, Northeast University of Technology, Shenyang 110006, China. INFLUENCE OF MnO ON REDUCTION OF TiO_2 IN BLAST FURNACE TYPE SLAG [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(7): 1-7.
[5]	LIU Huanming DU Hong Benxi Iron and Steel Company,Benxi,ChinaYANG Zupan Northeast University of Technology,Shenyang,ChinaLI Guodong DU Kun Centrel Iron and Steel Research Institute,Ministry of Metallurgical Industry,Beijing,China. ACTIVITY OF TiO_2 IN MOLTEN BLAST FURNACE SLAG [J]. Acta Metallurgica Sinica (English Letters), 1992, 5(10): 274-279.

THE STUDY ON BEHAVIOR OF Al 2O 3 C BRICK FOR BLAST FURNACE AT HIGH TEMPERATURE

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 5

Recommended Articles

Metrics

Comments