Abstract: The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.

Key words: Ni_3Al bearing Zr alloy, liquation cracking, hot ductility test