Influence of Continuous Bending Process on Texture Evolution and Mechanical Properties of AZ31 Magnesium Alloy

doi:10.1007/s40195-017-0671-7

Acta Metallurgica Sinica (English Letters) ›› 2018, Vol. 31 ›› Issue (3): 225-233.DOI: 10.1007/s40195-017-0671-7

所属专题： 2017-2018镁合金专辑； 2018镁合金专辑

收稿日期:2017-11-15 修回日期:2017-11-15 出版日期:2018-03-15 发布日期:2018-03-19

Influence of Continuous Bending Process on Texture Evolution and Mechanical Properties of AZ31 Magnesium Alloy

Ting-Zhuang Han^1,², Guang-Sheng Huang^1,^2,³(), Lun Huang^1,², Bin Jiang^1,^2,³, Guan-Gang Wang^1,², Ai-Tao Tang^1,^2,³, Fu-Sheng Pan^1,^2,³

1 State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China
2 National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, China
3 Chongqing Research Center for Advanced Materials,Chongqing Academy

Received:2017-11-15 Revised:2017-11-15 Online:2018-03-15 Published:2018-03-19

摘要/Abstract

Abstract:

Mg-3Al-1Zn alloy sheets have been deformed by continuous bending (CB) to investigate the effects of processing parameters (bending angle and repetitive passes) on the texture and formability. The samples exhibited a bimodal microstructure with abnormal growth grains in the surface region and fine grains distributed in the center after CB process followed by annealing. The texture evolution measured by XRD indicated that the basal poles were rotated from ND toward RD, and the texture intensity decreased with the bending angle decreasing and repetitive passes increasing. Compared with the as-received sample, the yield strength of CBA-120-2 sample significantly decreased from 183 to 112 MPa, and a smaller r-value and a larger n-value were obtained. The formability of CB processed samples in annealing condition was significantly enhanced with the highest of Erichsen value of 5.4 mm, increased by about 135%. The improvement of formability was likely attributed to the weakened and RD-tilt basal texture and coarse grains in the surface part.

Key words: Magnesium alloy, Continuous bending, Microstructure, Texture Stretch formability

. [J]. Acta Metallurgica Sinica (English Letters), 2018, 31(3): 225-233.

Ting-Zhuang Han, Guang-Sheng Huang, Lun Huang, Bin Jiang, Guan-Gang Wang, Ai-Tao Tang, Fu-Sheng Pan. Influence of Continuous Bending Process on Texture Evolution and Mechanical Properties of AZ31 Magnesium Alloy[J]. Acta Metallurgica Sinica (English Letters), 2018, 31(3): 225-233.

图/表 10

Fig. 1 Schematic diagram of a continuous bending device

Fig. 2 a Optical microstructure, b (0002) pole figure of as-received sample

Fig. 3 Microstructures of sheets in different regions. a I region, b II region, c III region during CB-120-1 process

Fig. 4 Microstructures of a CBA-140-1, b CBA-120-1, c CBA-120-2 samples

Fig. 5 The (0002) pole figures of a CBA-140-1, b CBA-120-1, c CBA-120-2 samples

Fig. 6 True stress-strain curves of different samples

Table 1 Mechanical properties of various samples

Samples	YS (MPa)			UTS (MPa)			FE (%)
Samples	RD	45°	TD	RD	45°	TD	FE (%)
AS	183 ± 2	200 ± 3	216 ± 1	334 ± 5	323 ± 7	330 ± 10	16.5 ± 0.5
CBA-140-1	140 ± 1	165 ± 2	196 ± 1	328 ± 5	321 ± 8	336 ± 7	18.2 ± 0.5
CBA-120-1	127 ± 2	157 ± 1	191 ± 3	315 ± 6	303 ± 5	331 ± 7	17.8 ± 0.5
CBA-120-2	112 ± 1	151 ± 1	186 ± 2	311 ± 4	307 ± 3	313 ± 6	19.2 ± 0.5

Fig. 7 Lankford values (r-value) and strain hardening exponent values (n-value) of various samples

Fig. 8 Average values of IE of various samples

Fig. 9 SEM images of the tensile fracture surface of a AS, b CBA-140-1, c CBA-120-1, d CBA-120-2 samples

参考文献

[1]	L. Zheng, H. Nie, W. Liang, H. Wang, Y. Wang, J. Magnes. Alloys 4, 115-122(2016)
[2]	I. Aatthisugan, A.R. Rose, D.S. Jebadurai, J. Magnes. Alloys 5(1), 20-25(2017)
[3]	H. Zhang, Y. Yan, J. Fan, W. Cheng, H.J. Roven, B. Xu, H. Dong, Mater. Sci. Eng. A 618, 540-545(2014)
[4]	J. Koike, T. Kobayashi, T. Mukai, H. Watanabe, M. Suzuki, K. Maruyama, K. Higashi, Acta Mater. 51, 2055-2065 (2003)
[5]	M. Mabuchi, Y. Chino, H. Iwasaki, Mater. Trans. 44, 490-495 (2003)
[6]	H. Zhang, G. Huang, J. Fan, H.J. Roven, B. Xu, H. Dong, J. Alloys Compd. 615, 302-310 (2014)
[7]	P. Liu, H. Jiang, Z. Cai, Q. Kang, Y. Zhang, J. Magnes. Alloys 4, 188-196(2016)
[8]	H. Zhang, Y. Liu, J. Fan, H.J. Roven, W. Cheng, B. Xu, H. Dong, J. Alloys Compd. 615, 687-692 (2014)
[9]	X. Huang, K. Suzuki, A. Watazu, I. Shigematsu, N. Saito, J. Alloys Compd. 479, 726-731 (2009)
[10]	X. Huang, K. Suzuki, A. Watazu, I. Shigematsu, N. Saito, J. Alloys Compd. 470, 263-268 (2009)
[11]	Y. Chino, K. Sassa, A. Kamiya, M. Mabuchi, Mater. Sci. Eng. A 473, 195-200(2008)
[12]	H. Zhang, G. Huang, L. Wang, H.J. Roven, F. Pan, J. Alloys Compd. 575, 408-413 (2013)
[13]	J. Suh, J. Victoria-Hernandez, D. Letzig, R. Golle, S. Yi, J. Bohlen, W. Volk, J. Mater. Proc. Technol. 217, 286-293 (2015)
[14]	J. Suh, J. Victoria-Hernández, D. Letzig, R. Golle, W. Volk, Mater. Sci. Eng. A 669, 159-170(2016)
[15]	B. Song, G. Huang, H. Li, L. Zhang, G. Huang, F. Pan, J. Alloys Compd. 489, 475-481 (2010)
[16]	H. Zhang, Trans. Nonferrous Metal. Soc. 21, 844-850 (2011)
[17]	T.Z. Han, G.S. Huang, Y.G. Wang, Trans. Nonferrous Metal. Soc. 26, 2043-2050 (2016)
[18]	T. Han, G. Huang, Y. Wang, G. Wang, Y. Zhao, F. Pan, Prog. Nat. Sci. Mater. Int. 26, 97-102 (2016)
[19]	G. Huang, L. Wang, H. Zhang, Y. Wang, Z. Shi, F. Pan, Mater. Lett. 98, 47-50 (2013)
[20]	L. Wang, G. Huang, H. Zhang, Y. Wang, L. Yin, J. Mater. Proc. Technol. 213, 844-850 (2013)
[21]	M.R. Barnett, Scr. Mater. 59, 696-698 (2008)
[22]	M. Barnett, Z. Keshavarz, A. Beer, D. Atwell, Acta Mater. 52, 5093-5103 (2004)
[23]	M. Knezevic, A. Levinson, R. Harris, R.K. Mishra, R.D. Doherty, S.R. Kalidindi, Acta Mater. 58, 6230-6242 (2010)
[24]	T. Al-Samman, G. Gottstein, Mater. Sci. Eng. A 490, 411-420(2008)
[25]	M. Kavyani, G.R. Ebrahimi, M. Sanjari, M. Haghshenas, J. Magnes. Alloys 4, 89-98(2016)
[26]	Y. Takayama, J.A. Szpunar, Mater. Trans. 42, 2050-2058 (2001)
[27]	G.-S. Huang, H. Zhang, X.-Y. Gao, B. Song, L. Zhang, Trans. Nonferrous Metal. Soc. 21, 836-843 (2011)
[28]	Z.-Y. Liu, T.-T. Huang, W.-J. Liu, S. Kang, Trans. Nonferrous Metal. Soc. 26, 378-389 (2016)
[29]	F. Guo, D. Zhang, X. Yang, L. Jiang, S. Chai, F. Pan, Mater. Sci. Eng. A 607, 383-389(2014)
[30]	W.P. Jia, X.D. Hu, H.Y. Zhao, D.Y. Ju, D.L. Chen, J. Alloys Compd. 645, 70-77 (2015)
[31]	Y. Zou, L. Zhang, H. Wang, X. Tong, M. Zhang, Z. Zhang, J. Alloys Compd. 669, 72-78 (2016)
[32]	T. Zhou, Z. Yang, D. Hu, T. Feng, M. Yang, X. Zhai, J. Alloys Compd. 650, 436-443 (2015)
[33]	H. Zhang, G. Huang, L. Wang, H.J. Roven, Z. Xu, F. Pan, Scr. Mater. 69, 49-52 (2013)
[34]	G. Mann, J. Griffiths, C. Cáceres, J. Alloys Compd. 378, 188-191 (2004)
[35]	S.R. Agnew, ?. Duygulu, Int. J. Plast. 21, 1161-1193 (2005)
[36]	Z. Li, J. Dong, X.Q. Zeng, C. Lu, W.J. Ding, Mater. Sci. Eng. A 466, 134-139(2007)
[37]	F. Lu, A. Ma, J. Jiang, J. Chen, D. Song, Y. Yuan, J. Chen, D. Yang, J. Alloys Compd. 643, 28-33 (2015)
[38]	Q. Yang, B. Jiang, X. Li, H. Dong, W. Liu, F. Pan, J. Magnes. Alloys 2, 8-12(2014)

Influence of Continuous Bending Process on Texture Evolution and Mechanical Properties of AZ31 Magnesium Alloy

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 10

参考文献

相关文章 0

编辑推荐

Metrics

本文评价