SURFACE TENSION OF MOLTEN IF STEEL CONTAINING Ti AND ITS INTERFACIAL PROPERTIES WITH SOLID ALUMINA

L.C.Zhong   

  • Received:1900-01-01 Revised:1900-01-01 Online:2004-12-25 Published:2009-10-10
  • Contact: L.C.Zhong

Abstract: Surface tension of molten IF steel containing Ti and contact angle between the liquid steel and solid alumina were measured with sessile droplet method under Ar gas atmosphere at 1500, 1575 and 1600℃. The results show that titanium decreases the surface tension of themolten IF steel and the contact angle. The interfacial tension between the molten IF steel containing Ti and solid alumina decreases with increase in titanium content. The work of adhesion between molten IF steel containing Ti and solid alumina decreases slightly at1550~C, but increases at 1600℃ with increasing titanium content. It can be deduced that fine bubbles and fine alumina inclusions are easily entrapped in solidifying interface for IF steel containing Ti.

Key words: surface tension, contact angle, molten IF steel