Acta Metallurgica Sinica (English Letters) ›› 2004, Vol. 17 ›› Issue (3): 247-254 .

• Research Articles • Previous Articles     Next Articles

Microbridge Testing of Young's Modulus and Residual Stress of Nickel Film Electroplated on Silicon Wafer

Y. Zhou, C.S. Yang, J.A. Chen, G.F. Ding, L. Wang, M.J. Wang, Y.M. Zhang and T.H. Zhang   

  • Received:1900-01-01 Revised:1900-01-01 Online:2004-06-25 Published:2009-10-10

Abstract: Microbridge testing is used to measure the Young's modulus and residual stresses of metallic films. Nickel film microbridges with widths of several hundred microns are fabricated by Microelectromechanical Systems. In order to measure the mechanical properties of nickel film microbridges, special shaft structure is designed to solve the problem of getting the load-deflection curves of metal film microbridge by Nanoindenter XP system with normal Berkovich probe. Theoretical analysis of the microbridge load-deflection curve is proposed to evaluate the Young's modulus and residual stress of the films simultaneously. The calculated results based on the experimental measurements show that the average Young's modulus and residual stress are around 190GPa and 175MPa respectively, while the Young's modulus measured by Nano- hardness method on nickel film with silicon substrate is 186.8±7.34GPa.

Key words: nickel film microbridge, MEMS, mechanical property, load- deflection measurement