Electrochemical Characteristics in Seawater for Cold Thermal Spray-Coated Al-Mg Alloy Layer

doi:10.1007/s40195-016-0437-7

摘要/Abstract

Abstract:

For corrosion protection of carbon steel in a marine environment, cold arc thermal spray coating was applied to the surface with Al and Al-Mg alloy wires. The surface hardness of Al and Al-Mg thermal spray coatings increased with Mg content. And the various electrochemical experiments were carried out to evaluate corrosion damage characteristics of the thermal spray coating layers. The Al and Al-Mg thermal spray coating layers presented negative potentials compared to carbon steel in corrosion potential measurements. And an anodic polarization experiment revealed a tendency of activation polarization with no passivation. Furthermore, the corrosion damage of the thermal spray coating layer in galvanostatic experiment was observed mainly at the defect area, and the Al-3Mg thermal spray coating layer presented less surface damages than others. In addition, the Al-3Mg thermal spray coating layer showed the lowest corrosion rate while having a sufficient driving voltage for cathodic corrosion protection. Therefore, it is an optimal thermal spray material for sacrificial anode.

Key words: Corrosion protection, Carbon steel, Arc thermal spray coating, Al-Mg alloy, Marine environment

. [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(8): 727-734.

Il-Cho Park,Seong-Jong Kim. Electrochemical Characteristics in Seawater for Cold Thermal Spray-Coated Al-Mg Alloy Layer[J]. Acta Metallurgica Sinica (English Letters), 2016, 29(8): 727-734.

图/表 9

Fig. 1 Cross-sectional morphologies of the thermal sprayed coating layers: a Al, b Al-3Mg, c Al-5Mg

Fig. 2 Corrosion potential measurements of SS400 and thermal sprayed coating layers in seawater

Fig. 3 Anodic polarization curves of thermal sprayed coating layers in seawater

Fig. 4 Surface morphologies of thermal sprayed coating layers after anodic polarization experiment in seawater: a SEM analysis, b 3D analysis

Fig. 5 Cathodic polarization curves of thermal sprayed coating layers in seawater

Fig. 6 Results of Tafel analysis of thermal sprayed coating layers in seawater

Fig. 7 Surface morphologies of thermal sprayed coating layers with galvanostatic experiment in seawater

参考文献

[1]	D. Chaliampalias, G. Vourlias, E. Pavlidou, G. Stergioudis, S. Skolianos, K. Chrissafis, Appl. Surf. Sci. 255, 3104(2008)
[2]	W. Tian, Y. Wang, T. Zhang, Y. Yang, Mater. Chem. Phys. 118, 37(2009)
[3]	X. Zhao, D. Yan, S. Li, C. Lu, Appl. Surf. Sci. 257, 10078(2011)
[4]	G. Jandin, H. Liao, Z.Q. Feng, C. Coddet, Mater. Sci. Eng.,A 349, 298 (2003)
[5]	Y. Xiao, X. Jiang, Y. Xiao, L. Ma, Procedia Eng. 27, 1644(2012)
[6]	H. Katayama, S. Kuroda, Corros. Sci. 76, 35(2013)
[7]	J. Davis ( Ohio, 1999)
[8]	H. Ezuber, A. El-Houd, F. El-Shawesh, Mater. Des. 29(4), 801(2008)
[9]	Y. Huang, Y. Li, Z. Xiao, Y. Liu, Y. Huang, X. Ren, J. Alloys Compd. 673, 73(2016)
[10]	C. Vargel, M. Jacques, M.P. Schmidt, Corrosion ofAluminum, 2nd edn. (Elsevier, Amsterdam, 2004), pp. 221-225
[11]	D. Zander, C. Schnatterer, C. Altenbach, V. Chaineux, Mater. Des. 83, 49(2015)
[12]	R.K. Gupta, N.L. Sukiman, M.K. Cavanaugh, B.R.W. Electrochim. Acta 66, 245 (2012)
[13]	Y. Wang, R.K. Gupta, N.L. Sukiman, R. Zhang, C.H.J. Corros. Sci. 73, 181(2013)
[14]	Y. Tao, T. Xiong, C. Sun, L. Kong, X. Cui, T. Li, G.L. Song, Corros. Sci. 52, 3191(2010)
[15]	T. Kaewmaneekul, G. Lothongkum, Corros. Sci. 66, 67(2013)
[16]	L. Abdoli, J. Huang, H. Li, Mater. Chem. Phys. 173, 62(2016)
[17]	S.J. Kim, S.K. Jang, J. Korean Soc. Mar. Eng. 33, 313(2009)
[18]	J.S. Kim, H.S. Kim, J. Korean Inst. Surf. Eng. 39, 25(2006)
[19]	Standard by National Association of Corrosion Engineers (NACE SP0169-2007, Houston, 2007), pp. 12-14
[20]	R.A. Gummow, Mater. Perform. 32, 21(1993)
[21]	M. Pourbaix, Atlas of Electrochemical Equilibria in Aqueous Solution (NACE, Houston, 1974), pp. 139-145
[22]	D. Apelian, B.H. Kear, H.W. Schadler, Spray Deposition Process in Rapidly Solidified Crystalline Alloys (The Metallurgical Society, Pennsylvania, 1985), pp. 93-709
[23]	Y.K. Park, G.S. Choi, D.H. Lee, Korean J. Mater. Res. 2, 85(1992)
[24]	D.A. Jones, Principles and Prevention of Corrosion, 2nd edn. (Prentice Hall, Upper Saddle River, 2011), pp. 75-98
[25]	J.F. Yan, T.V. Nguyen, R.E. White, J. Electrochem. Soc. 140, 733(1993)
[26]	W. Sun, G. Liu, L. Wang, Y. Li, Electrochim. Acta 78, 597 (2012)
[27]	C. Rousseau, F. Baraud, L. Leleyter, M. Jeannin, O. Gil, Corros. Sci. 52, 2206(2010)
[28]	Ch. Barchiche, Electrochim. Acta 54, 3580 (2009)
[29]	K. Spencer, D.M. Fabijanic, M.X. Zhang, Surf. Coat. Technol. 204, 336(2009)
[30]	M.M. Verdian, K. Raeissi, M. Salehi, Corros. Sci. 52, 1052(2010)
[31]	V.R.S.S. Brito, I.N. Bastos, H.R.M. Mater. Des. 41, 282(2012)
[32]	J.A. Lyndon, R.K. Gupta, M.A. Gibson, N. Birbilis, Corros. Sci. 70, 290(2013)
[33]	M.M. Sharma, J.D. Tomedi, J.M. Parks, Corros. Sci. 93, 180(2015)
[34]	M.C. Reboul, T.J. Warner, H. Mayet, B. Baroux, Corros. Rev. 15, 471(1997)
[35]	I.L. Rosenfeld, I.K. Marshakov, Corrosion 20, 115 (1964)
[36]	A. Aballe, M. Bethencourt, F.J. Botana, M.J. Cano, M. Marcos, Corros. Sci. 45, 161(2003)
[37]	Y.W. Kim, J.G. Kim, Korean J. Met. Mater. 38, 918(2000)