Influence of Extrusion Joint on Microstructural Evolution and Properties of Mg Alloy Sheet

doi:10.1007/s40195-016-0411-4

金属学报英文版 ›› 2016, Vol. 29 ›› Issue (5): 475-482.DOI: 10.1007/s40195-016-0411-4

所属专题： 2016-2017镁合金虚拟专辑

收稿日期:2016-04-08 修回日期:2016-04-08 出版日期:2016-04-08 发布日期:2016-05-10

Influence of Extrusion Joint on Microstructural Evolution and Properties of Mg Alloy Sheet

Qing-Shan Yang^1,²(), Zu-Jian Yu¹, Hu-Cheng Pan³, Qing-Wei Dai¹, Jian-Hui Li¹

1 .School of Metallurgy and Materials Engineering, Chongqing University of Science and Technology, Chongqing 401331,China
2. Chongqing Academy of Science and Technology,Chongqing 401123, China
3. Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern;

Received:2016-04-08 Revised:2016-04-08 Online:2016-04-08 Published:2016-05-10

摘要/Abstract

Abstract:

The mechanical behaviour of AZ31 magnesium alloy sheet with the extrusion joint (EJ) was evaluated. Extruded joint of AZ31 alloy sheets was obtained by the hot extrusion process. Tensile tests were carried out along the extrusion direction at room temperature, and both the non-uniform plastic deformation and the fracture behaviour were studied. It is found that the samples with EJ present significantly deteriorated mechanical properties compared with the EJ-free counterpart. Inhomogeneous microstructure distribution around EJ zone brings in the uncoordinated deformation due to the high density of \(\{ 10\bar{1}2\}\) twins which were readily activated during plastic deformation.

Key words: Mg alloy, Microstructure, Twin, Texture, Extrusion joint

. [J]. 金属学报英文版, 2016, 29(5): 475-482.

Qing-Shan Yang, Zu-Jian Yu, Hu-Cheng Pan, Qing-Wei Dai, Jian-Hui Li. Influence of Extrusion Joint on Microstructural Evolution and Properties of Mg Alloy Sheet[J]. Acta Metallurgica Sinica (English Letters), 2016, 29(5): 475-482.

图/表 11

Fig. 1 Schematic diagram of the samples for the tensile tests

Fig. 2 Optical microstructure and (0002) pole figure of AZ31 alloy sheet

Fig. 3 Optical microstructure of the extrusion joint (EJ) sample at the joint zone

Fig. 4 Optical microstructures of the joint zone at top a and middle b layers

Fig. 5 EBSD results of the microstructure and the misorientation distribution for AZ31 alloy sheet

Fig. 6 True stress-strain response of AZ31 alloy sheets

Table 1 Tensile properties of the AZ31 alloy sheet

Sample	YS	(MPa)	UTS	(MPa)	FE(%)
I	(without	EJ)	184	268	12.6
II	(with	EJ)	197	252	6.9

Fig. 7 Work-hardening (WH, θ) behaviour of the sample I and II

Fig. 8 Optical micrographs of fractured tensile samples: near the fracture surface a and away from the fracture surface b of the sample I; the joint zone c and near the fracture surface d of sample II

Fig. 9 EBSD maps of the fractured tensile samples

Fig. 10 Tensile fracture morphologies of the sample I (a, b, c) and sample II (d, e, f). (g) Near the fracture surface morphology of sample II. Energy dispersive spectroscopy (EDS) analysis of points (p1 and p2)

参考文献 38

[1]	S. Liu, G. Yang, W. Jie, Acta Metall. Sin. (Engl. Lett.) 27, 1134(2014)
[2]	X.H. Chen, L.Z. Liu, J. Liu, F.S. Pan, Acta Metall. Sin. (Engl.Lett.) 28, 492(2015)
[3]	S. Seipp, M.F.X. Int. J. Plast. 35, 155(2012)
[4]	A.A. Luo, J. Magn. Alloys 1, 2 (2013)
[5]	L. Wang, G. Huang, Q. Quan, P. Bassani, E. Mostaed, M. Vedani, F. Pan, Mater. Design 63, 177 (2014)
[6]	M.R. Barnett, Z. Keshavarz, A.G. Beer, D. Atwell, Acta Mater.52, 5093(2004)
[7]	Q.S. Yang, B. Jiang, Y. Tian, W.J. Liu, F.S. Pan, Mater. Lett.100, 29(2013)
[8]	D.-H. Hou, S.-M. Liang, R.-S. Chen, C. Dong, E.-H. Han, Acta Metall. Sin. (Engl. Lett.) 28, 115(2014)
[9]	Q.S. Yang, B. Jiang, Z.J. Yu, Q.W. Dai, S.Q. Luo, Acta Metall. Sin. (Engl. Lett.) 28, 1257(2015)
[10]	X. Yu, B. Jiang, H. Yang, Q. Yang, X. Xia, F. Pan, Appl. Surf. Sci. 353, 1013(2015)
[11]	M. Yuasa, M. Hayashi, M. Mabuchi, Y. Chino, Acta Mater. 65,207(2014)
[12]	Y.C. Yuan, A.B. Ma, J.H. Jiang, Y. Sun, F.M. Lu, L.Y. Zhang,D. Song, J. Alloys Compd. 594, 182(2014)
[13]	J. Dai, B. Jiang, X. Li, Q. Yang, H. Dong, X. Xia, F. Pan, J.Alloys Compd. 619, 411(2015)
[14]	H. Pan, G. Qin, M. Xu, H. Fu, Y. Ren, F. Pan, Z. Gao, C. Zhao,Q. Yang, J. She, B. Song, Mater. Design 83, 736 (2015)
[15]	G.S. Song, S.H. Zhang, L. Zheng, L. Ruan, J. Alloys Compd.509, 6481(2011)
[16]	M.N. Mekonen, D. Steglich, J. Bohlen, D. Letzig, J. Mosler, Mater. Sci. Eng. A 540, 174 (2012)
[17]	J. He, B. Jiang, Q. Yang, X. Li, X. Xia, F. Pan, J. Alloys Compd.621, 301(2015)
[18]	C. Chen, T. Liu, C. Lv, L. Lu, D. Luo, Mater. Sci. Eng. A 539,223 (2012)
[19]	H. Zhang, G. Huang, J. Fan, H.J. Roven, F. Pan, B. Xu, Mater.Sci. Eng. A 608, 234 (2014)
[20]	B. Zhang, Y. Wang, L. Geng, C. Lu, Mater. Sci. Eng. A 539, 56 (2012)
[21]	S.M. Arab, A. Akbarzadeh, J. Magn. Alloys 1, 145 (2013)
[22]	N.V. Dudamell, I. Ulacia, F. Ga´lvez, S. Yi, J. Bohlen, D. Letzig,I. Hurtado, M.T. Mater. Sci. Eng. A 532, 528(2012)
[23]	I. Ulacia, N.V. Dudamell, F. Ga´lvez, S. Yi, M.T. Acta Mater. 58, 2988(2010)
[24]	W.C. Zhang, Y. Yu, X.N. Zhang, W.Z. Chen, E.D. Wang,Mater. Sci. Eng. A 600, 181 (2014)
[25]	D. Liu, R. Xin, X. Zheng, Z. Zhou, Q. Liu, Mater. Sci. Eng. A 561, 419 (2013)
[26]	J.A. del Valle, F. Carren˜o, O.A. Ruano, Acta Mater. 54, 4247(2006)
[27]	Q. Yang, B. Jiang, W. Jiang, S. Luo, F. Pan, Mater. Sci. Eng. A628, 143(2015)
[28]	Z. Zhang, E.F. Rauch, M. Ve´ron, Mater. Lett. 111, 192(2013)
	Q.-S. Yanget al.: Acta Metall. Sin. (Engl. Lett.), 2016, 29(5), 475-482 481
[29]	R. Xin, C. Guo, Z. Xu, G. Liu, X. Huang, Q. Liu, Scr. Mater. 74,96(2014)
[30]	S.M. Razavi, D.C. Foley, I. Karaman, K.T. Hartwig, O. Duygulu,L.J. Kecskes, S.N. Mathaudhu, V.H. Hammond, Scr.Mater. 67, 439(2012)
[31]	B. Song, R. Xin, G. Chen, X. Zhang, Q. Liu, Scr. Mater. 66,1061(2012)
[32]	D. Sarker, D.L. Chen, Scr. Mater. 67, 165(2012)
[33]	B. Song, N. Guo, T. Liu, Q. Yang, Mater. Design 62, 352 (2014)
[34]	A. Styczynski, C. Hartig, J. Bohlen, D. Letzig, Scr. Mater. 50,943(2004)
[35]	M. Knezevic, A. Levinson, R. Harris, R.K. Mishra, R.D. Doherty,S.R. Kalidindi, Acta Mater. 58, 6230(2010)
[36]	B. Wang, R. Xin, G. Huang, Q. Liu, Mater. Sci. Eng. A 534, 588(2012)
[37]	X. Li, T. Al-Samman, G. Gottstein, Mater. Design 32, 4385(2011)
[38]	N. Stanford, J. Geng, Y.B. Chun, C.H.J. Acta Mater. 60, 218(2012)

Influence of Extrusion Joint on Microstructural Evolution and Properties of Mg Alloy Sheet

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 11

参考文献 38

相关文章 0

编辑推荐

Metrics

本文评价